纳米金-聚二甲基硅氧烷复合薄膜制备及电学特性研究

发布时间：2018-07-05 18:38

  本文选题：AuNPs-PDMS + 微薄膜　； 参考：《化工新型材料》2017年07期

【摘要】：纳米金-聚二甲基硅氧烷(AuNPs-PDMS)复合微薄膜具有良好的生物适应性和较高的灵敏度,可作为生物传感器的敏感元件。通过两步还原法制得的AuNPs-PDMS复合微薄膜,具有良好的导电性和柔韧性。通过温度、形变、膜厚对复合薄膜导电性影响进行测试研究,结果表明转速为1000r/min时,复合薄膜电阻最小,为7.3Ω;在施加3kPa气压时,复合薄膜表现出半导体特性,最大电阻变化率为0.022%;复合薄膜的电阻随温度的升高而增大,符合线性关系。
[Abstract]:AuNPs-PDMS composite microfilm has good biological adaptability and high sensitivity, and can be used as a sensitive element of biosensor. AuNPs-PDMS composite microfilms prepared by two-step reduction method have good conductivity and flexibility. The effects of temperature, deformation and film thickness on the electrical conductivity of the composite film were investigated. The results show that the resistance of the composite film is the smallest (7.3 惟) when the rotational speed is 1000r/min, and the composite film exhibits semiconductor properties when the pressure is 3 KPA. The change rate of the maximum resistance is 0.0222.The resistance of the composite film increases with the increase of temperature, which is in line with the linear relationship.
【作者单位】： 太原理工大学微纳系统研究中心新型传感器与智能控制教育部和山西省重点实验室;
【基金】：国家自然科学基金(61471255,61474079) 863项目(2013AA041109,2015AA042601)
【分类号】：TB383.2;TP212.3

【相似文献】

相关期刊论文 前10条

1 高新来,潘慧铭,王跃林,李和昌,李万华;α,ω-二丁酮肟基聚二甲基硅氧烷和α,ω-二(N-甲基乙酰胺基)聚二甲基硅氧烷的表征[J];有机硅材料;2001年02期

2 ;端羟基聚二甲基硅氧烷制备的改进[J];有机硅材料;2004年04期

3 金美花;廖明义;江雷;;超疏水性聚二甲基硅氧烷膜的制备及其表面吸附性研究[J];高等学校化学学报;2007年05期

4 余世诚,徐种德;聚二甲基硅氧烷在混合溶剂中的粘度和光散射[J];高分子通讯;1964年06期

5 应琦琮,朱丽，

本文编号：2101331