电沉积制备汽车用高硬度镍-钨合金薄膜

发布时间：2018-10-17 22:30

【摘要】：使用电沉积技术在汽车软钢材料上电镀高硬度镍-钨合金薄膜。研究发现,镍-钨合金属于诱导共沉积。提高镀液中钨酸钠的浓度,有利于增大合金中钨的质量分数,从而显著提高合金的硬度。镍为面心立方结构,钨为体心立方结构,最终异常共沉积生成的Ni17W3是一种固溶体。钨原子占据了镍原子的晶格,形成晶格畸变。合金中钨的质量分数越高,晶格畸变越明显,有利于细化晶粒、降低粗糙度,从而提高合金的机械性能。
[Abstract]:Electroplating of high-hardness nickel-tungsten alloy film on automobile soft steel by electrodeposition technology. It is found that nickel-tungsten alloy belongs to induced codeposition. Increasing the concentration of sodium tungstate in the plating solution is beneficial to increase the mass fraction of tungsten in the alloy and thus increase the hardness of the alloy. Nickel is a face-centered cubic structure and tungsten is a body-centered cubic structure. Finally, Ni17W3 formed by anomalous co-deposition is a solid solution. Tungsten atoms occupy the lattice of nickel atoms and form lattice distortion. The higher the mass fraction of tungsten in the alloy is, the more obvious the lattice distortion is, which is beneficial to refine the grain size and reduce the roughness, thus improving the mechanical properties of the alloy.
【作者单位】： 河南工程学院;
【分类号】：TB383.2;TQ153

【相似文献】

相关期刊论文 前10条

1 曾德贵;文帝武;;在钨及钨合金上电镀黑镍[J];电镀与精饰;1992年06期

2 王琏 ,李增贵;钨及钨合金的电镀[J];化学世界;1948年03期

3 胡家璜;;对于带有镍钼粘合剂的无钨合金废料的处理[J];钼业经济技术;1990年03期

4 张世民;铁基镍钴钨合金阴极的研究[J];应用化学;1987年06期

5 万小波;张林;周兰;肖江;;电镀非晶态镍钨合金工艺研究[J];材料保护;2006年12期

6 卢维昌,李兆军,王春福;不同基底非晶态镍钨合金电沉积中氢的作用[J];化工冶金;1998年01期

7 白德林,李凤琴,田汝珉;电沉积钴-钨合金的工艺试验[J];油田地面工程;1996年04期

8 黄令,董浚修,杨防祖,许书楷,周绍民;镍钨合金电沉积伏安特性和初期行为的研究[J];电镀与涂饰;1999年01期

9 章善彪;谭业发;谭华;蔡文利;李华兵;;油润滑对镍钨合金刷镀层摩擦学性能的影响[J];润滑与密封;2008年10期

10 陈海春;;双波长K系数分光光度法测定镍钨合金镀液中的钨含量[J];材料保护;2012年05期

相关会议论文 前1条

1 何凤姣;高晖;;Yc-4型钨合金环保电镀新工艺取代镀铬在液压件表面加工上的应用[A];2005'（贵阳）表面工程技术创新研讨会论文集[C];2005年

相关硕士学位论文 前4条

1 刘爽;镍钨合金电沉积工艺研究[D];哈尔滨工业大学;2016年

2 张颖;钨合金镀层性能及其发黑研究[D];湖南大学;2010年

3 王秀敏;电镀钨合金耐H_2S腐蚀研究及脉冲电沉积钨合金[D];湖南大学;2009年

4 高雷;代铬电沉积镍—铁—钨合金的研究[D];山东大学;2011年

，

本文编号：2278227