Inter-granular exchange coupling and magnetic anisotropy of
发布时间：2021-06-03 20:23
In the present work, a series of Ta/Ru/Co-23 at%Pt thin films with varied Ru underlayer thicknesses were fabricated by magnetron sputtering. All of the films show c-axis preferred orientation perpendicular to the film surface. The drop of c/a ratio and lattice expansion of Co–Pt layer with the increase in Ru underlayer thickness was revealed by X-ray diffraction（XRD）. The coercivity of the Ta/Ru/Co–Pt thin films increases drastically with Ru underlayer thickness increasing, due to the enhancemen...
【文章来源】：Rare Metals. 2016,35(06)EISCICSCD
【文章页数】：8 页
【参考文献】：
期刊论文
[1]Effect of Phosphor Addition on Intergranular Exchange Coupling of Co-Pt Thin Films[J]. Bo Yang1), Gaowu Qin1), Wenli Pei1), Song Li1), Yuping Ren1) and Shunji Ishio2) 1) Key Laboratory for Anisotropy & Texture of Materials, Northeastern University, Shenyang 110004, China 2) Department of Material Science & Engineering, Akita University, Akita 0108502, Japan. Journal of Materials Science & Technology. 2011(05)
本文编号：3211194
【文章来源】：Rare Metals. 2016,35(06)EISCICSCD
【文章页数】：8 页
【参考文献】：
期刊论文
[1]Effect of Phosphor Addition on Intergranular Exchange Coupling of Co-Pt Thin Films[J]. Bo Yang1), Gaowu Qin1), Wenli Pei1), Song Li1), Yuping Ren1) and Shunji Ishio2) 1) Key Laboratory for Anisotropy & Texture of Materials, Northeastern University, Shenyang 110004, China 2) Department of Material Science & Engineering, Akita University, Akita 0108502, Japan. Journal of Materials Science & Technology. 2011(05)
本文编号：3211194
本文链接：https://www.wllwen.com/guanlilunwen/gongchengguanli/3211194.html