1Cr11MoNiWVNbN不锈钢氮化组织异常原因分析及解决措施

发布时间：2018-01-03 19:41

本文关键词：1Cr11MoNiWVNbN不锈钢氮化组织异常原因分析及解决措施　出处：《热加工工艺》2017年18期 　论文类型：期刊论文

【摘要】：对1Cr11MoNiWVNbN不锈钢在600℃气体氮化过程中出现的黑色条纹进行了深入研究。结果表明:黑色条纹不是裂纹,而是一种异常组织。分析这种异常组织出现的原因是和γ'相的存在、碳原子远程迁移、硬度落差、腐蚀剂作用下的电化学作用、冷却介质等有密切联系;提出在625℃氮化、640℃退氮、在氮气保护气氛中冷却的气体氮化方法,获得了层深0.36~0.39mm,硬度798HV,脆性1级,无黑色条纹的渗层。并从理论上解释了这种氮化方法不产生黑色条纹的原因。
[Abstract]:To appear at 600 DEG C during gas nitriding of 1Cr11MoNiWVNbN stainless steel black stripes were studied. The results showed that the black stripe is not a crack, but a kind of abnormal tissue. The causes of the abnormal tissue is and gamma phase, carbon atom migration distance, hardness drop, electrochemical corrosion under the action of agent. There is close contact with the cooling medium; put forward at 625 C 640 C nitrogen nitriding, annealing, gas nitriding method of cooling in nitrogen atmosphere, the depth of 0.36~0.39mm, hardness 798HV, brittle layer 1, no black stripes. And theoretically explains why the nitriding method does not produce the black stripes..

【作者单位】：华电电力科学研究院山东分院;哈尔滨汽轮机厂有限责任公司;
【分类号】：TG142.71;TG156.82
【正文快照】： 对1Cr11Mo Ni WVNb N这种材料按照传统的不锈钢氮化温度600℃进行氮化处理后,在氮化试样和产品解剖件的金相检查中,不管是否腐蚀试样,均会在渗层表面、渗层中及过渡区发现有黑色条纹。这种黑色条纹近似平行于表面,如图1所示。这种黑色条纹疑似裂纹,从以下方面对其进行了分析。

【相似文献】