零卷吸条件下界面滑移的试验观察

发布时间：2018-03-14 04:13

  本文选题：零卷吸　切入点：界面滑移　出处：《润滑与密封》2017年09期 　论文类型：期刊论文

【摘要】：利用光干涉技术观察球-盘运动状态由纯滑动变为零卷吸后接触区内润滑油膜的变化特征,得出不同于经典理论的结果,并将其归因于界面滑移效应。对于可能导致界面滑移产生的润滑油极限剪应力和界面临界剪应力2种机制进行分析,认为界面临界剪应力可以合理解释试验现象。为进一步证实分析的正确性,追踪零卷吸条件下冲击封油核心的运动规律,试验结果与分析结果相吻合。对零卷吸和球纯滑条件下封油核心运动速度进行定量对比,结果显示润滑油内存在同一不可超越的临界剪应力,得出镀有铬膜的玻璃盘界面具有较低的临界剪应力。
[Abstract]:The characteristics of lubricating oil film in the contact region after pure sliding to zero entrainment are observed by using optical interference technique, and the results are different from the classical theory. The ultimate shear stress of lubricating oil and the critical shear stress of interface are analyzed. It is considered that the critical shear stress at the interface can reasonably explain the experimental phenomena. In order to further verify the correctness of the analysis, the motion law of the impingement sealing core under zero entrainment condition is traced. The experimental results are in good agreement with the analytical results. The results show that there exists the same insuperable critical shear stress in the lubricating oil under the conditions of zero entrainment and pure spherical slippage. The critical shear stress of the glass-disk interface coated with chromium film is lower.
【作者单位】： 青岛理工大学机械工程学院;
【基金】：国家自然科学基金项目(51405525,51275252) 山东省优秀中青年科学家奖励基金项目(BS2014ZZ004)
【分类号】：TH117.2

【相似文献】

相关期刊论文 前7条

1 刘建平;耿美香;郭峰;;零卷吸预跑合对一类反常弹流油膜的影响[J];润滑与密封;2007年08期

2 姜培刚;陈建军;耿美香;郭峰;;周期间歇卷吸条件下弹流油膜的实验[J];航空动力学报;2009年03期

3 谭洪恩;杨沛然;尹昌磊;;不同卷吸速度方向下的椭圆接触弹流乏油分析[J];煤矿机械;2008年01期

4 曲十月,郭峰,杨沛然;卷吸速度为任意方向的椭圆接触弹流润滑分析[J];润滑与密封;1999年04期

5 张建军;杨沛然;;变卷吸速度的点接触热弹流润滑分析[J];润滑与密封;2007年01期

6 贺惠农，周银生，傅连华，，全永听，韦云隆;挤压和卷吸效应耦合作用润滑机理的研究[J];浙江大学学报(自然科学版);1996年05期

7 王学锋;郭峰;胡如夫;尚伟燕;;大黏度润滑剂油膜形状实验测量[J];润滑与密封;2013年06期

相关硕士学位论文 前2条

1 张彬彬;零卷吸条件下弹流油膜表面凹陷现象研究[D];青岛理工大学;2015年

2 张林慧;变速条件下弹流油膜的瞬态响应[D];青岛理工大学;2010年

本文编号：1609553