35VB钢高强螺栓断裂失效分析

发布时间：2018-03-24 01:03

  本文选题：VB钢高强螺栓　切入点：断裂失效　出处：《热加工工艺》2017年18期

【摘要】：某风电机组用35VB钢高强螺栓发生断裂失效。应用直读光谱仪、拉伸试验机、冲击试验机、洛氏硬度计、金相显微镜、扫描电子显微镜等分析测试手段,对其进行了宏观形貌、化学成分、拉伸性能、冲击性能、楔负载、硬度、夹杂物、脱碳、微观组织等研究,分析了35VB钢高强螺栓断裂失效的原因,提出了预防和改进措施。结果表明:35VB钢高强螺栓断裂失效是该批次螺栓在制造过程中热处理工艺控制不当。此外,螺纹牙底存在半脱碳层,亦是螺栓的薄弱环节。
[Abstract]:The fracture failure of high strength bolt of 35VB steel used in a wind turbine unit was analyzed and tested by means of direct reading spectrometer, tensile tester, impact tester, Rockwell hardness tester, metallographic microscope, scanning electron microscope, etc. Chemical composition, tensile properties, impact properties, wedge loading, hardness, inclusions, decarburization, microstructure and so on were studied. The failure reasons of high strength bolts of 35VB steel were analyzed. The prevention and improvement measures are put forward. The results show that the failure of the high strength bolt of the steel w 35VB is the improper control of the heat treatment process during the manufacture of the batch bolt. In addition, there is a semi-decarburized layer on the bottom of the thread, which is also the weak link of the bolt.
【作者单位】： 环境保护部核与辐射安全中心;太原科技大学材料科学与工程学院;
【分类号】：TG142.15

【相似文献】

相关期刊论文 前10条

1 李桂芳;浅谈摩托车用高强螺栓的热处理[J];金属世界;2003年03期

2 陈斌强;;钢结构用10.9S扭剪型高强螺栓连接副紧固轴力偏低原因分析[J];理化检验(物理分册);2009年12期

3 郭寓岷,贺贤娟,刘广立;焊接——高强螺栓混合连接性能与工艺研究[J];钢结构;1996年03期

4 杨建祥;塔机高强螺栓专用扳手的设计[J];建筑机械;2003年07期

5 牛禧;张睿;许先果;;40Cr高强螺栓断裂原因分析[J];热加工工艺;2012年20期

6 彭成荫;;栓铆并用混合节点——设备检修的一项新工艺[J];武钢技术;1978年04期

7 张建国;;20MnTiB高强螺栓断裂原因分析[J];热处理技术与装备;2011年02期

8 丁建生;肖峰;肖杰;;35CrMoA钢风电高强螺栓热处理工艺研究[J];热加工工艺;2012年12期

9 王萍;;高强螺栓实物拉伸试验夹具的研制及应用[J];工程与试验;2013年03期

10 韩云程;无须热处理的高强螺栓用线材[J];天津冶金;1999年03期

相关会议论文 前1条

1 周金水;;宝钢化工公司希罗E-2201换热器法兰高强螺栓断裂原因分析及对策[A];2007年中国机械工程学会年会论文集[C];2007年

相关硕士学位论文 前3条

1 王刘涛;高强螺栓用42CrMo钢轧制工艺研究[D];安徽工业大学;2016年

2 张鹏飞;不同表面处理工艺对高强螺栓钢组织及性能的影响[D];西南交通大学;2017年

3 魏军;高强度螺栓失效研究与扭矩系数测定[D];华北电力大学;2014年

，

本文编号：1655985