乳胶泡沫引火位置对火蔓延特性的影响

发布时间：2018-06-17 13:01

  本文选题：火蔓延 + 泡沫　； 参考：《化工学报》2017年09期

【摘要】：利用自行搭建的小尺寸实验平台,开展了对不同点火位置的乳胶泡沫材料燃烧过程的对比实验,通过对火蔓延过程中的部分重要参数(如最大火焰高度、火蔓延速度和蔓延过程中样品表面温度变化等)的测定,分析了点火位置不同时,乳胶泡沫材料的火蔓延特性。结果表明:边缘点火和中间点火条件下,最大火焰高度分别为397和491 mm,火蔓延速度分别为1.8和0.97 mm·s~(-1);边缘点火时的乳胶泡沫材料表面火蔓延过程中的温度低于中间点火情况下。
[Abstract]:A comparative experiment on the combustion process of latex foam materials with different ignition positions was carried out by using a self built small size experimental platform. By measuring some important parameters in the process of fire spread, such as the maximum flame height, the velocity of fire spread and the temperature change of the sample surface during the spread process, the ignition position was analyzed. The fire spread characteristics of the foam material show that the maximum flame height is 397 and 491 mm respectively under the edge ignition and the intermediate ignition, and the fire spread speed is 1.8 and 0.97 mm s~ respectively (-1), and the temperature of the surface fire spread during the edge ignition is lower than that in the middle ignition.
【作者单位】： 中国计量大学质量与安全工程学院;浙江省家具检测技术研究重点实验室;喜临门家具股份有限公司;
【基金】：浙江省自然科学基金项目(17E060004) 浙江省大学生科研团队项目(2016R409047) 国家自然科学基金项目(51306168)~~
【分类号】：TQ317;X932

【相似文献】

相关期刊论文 前1条

1 殷弦;梁参军;程旭东;张瑞芳;张和平;;斜面角度对聚丙烯表面火蔓延的影响[J];消防科学与技术;2012年06期

相关博士学位论文 前2条

1 陈潇;表面朝向对典型固体可燃物着火特性及侧向火蔓延的影响研究[D];中国科学技术大学;2016年

2 彭飞;顶棚辐射与对流对PMMA热解及火蔓延的影响规律研究[D];中国科学技术大学;2016年

相关硕士学位论文 前2条

1 刘希平;典型热塑性材料逆流火蔓延及燃烧毒性研究[D];中国科学技术大学;2016年

2 柳爱静;风作用下聚苯乙烯保温材料逆流火蔓延行为研究[D];中国科学技术大学;2016年

，

本文编号：2031141