基于六硼化镧与壳聚糖的光热转换生物材料

发布时间：2018-01-05 05:23

本文关键词：基于六硼化镧与壳聚糖的光热转换生物材料　出处：《发光学报》2017年08期 　论文类型：期刊论文

【摘要】：为实现光合细菌(PSB)产氢过程的光分频利用,用六硼化镧(LaB_6)和壳聚糖制备了光热转换发光发热生物材料,研究了不同LaB_6纳米颗粒的生物材料在可见光下的吸光特性和光热转换特性。研究发现:该生物材料能较好地透过510~650 nm波长的光为PSB产氢供给光能,而其他波段的光用于激发LaB_6粒子产热为PSB提供热能。LaB_6纳米颗粒的吸光度及光热转换能力受颗粒尺寸影响显著,当生物材料中LaB_6颗粒平均水力直径为295 nm时,12 min内的温升速率为0.41℃/min,是载玻片的5.4倍。
[Abstract]:For the realization of photosynthetic bacteria (PSB) using optical frequency in the process of hydrogen production by six, lanthanum boron (LaB_6) and chitosan was prepared by photothermal conversion light-emitting heat biological material, the effect of different LaB_6 nanoparticles in biological materials in light absorption characteristics and photothermal conversion characteristics under visible light. The study found that: the creature the material can effectively through the 510~650 nm wavelength is PSB hydrogen supply of energy, while the other wavelengths for excitation of LaB_6 particle heat production and heat capacity of photothermal conversion provides absorbance of.LaB_6 nanoparticles was significantly affected by the particle size effect of PSB, when the average hydraulic LaB_6 particles in biological material with diameter of 295 nm, 12 min the temperature rise rate is 0.41 DEG /min, is 5.4 times the slides.

【作者单位】：重庆大学低品位能源利用技术及系统教育部重点实验室;重庆大学动力工程学院工程热物理研究所;重庆理工大学光纤传感与光电检测重庆市重点实验室重庆市现代光电检测技术与仪器重点实验室;
【基金】：国家自然科学基金委国际(地区)合作与交流项目(51561145013) 国家自然科学基金(51406020) 重庆市博士后科研项目(Xm2015070) 中央高校基本科研业务费(106112015CDJXY140003)资助项目~~
【分类号】：R318.08;TB34
【正文快照】： 3.重庆理工大学光纤传感与光电检测重庆市重点实验室重庆市现代光电检测技术与仪器重点实验室,重庆400054)1引言生物膜反应器应用于光生物制氢具有固定生物量较多、微生物的活性高、对周围环境中的生长抑制因素抗性强以及可重复利用等优点[1-3],被认为是一种有效的产氢强化方