共轭多孔聚合物薄膜的电化学制备及电容特性

发布时间：2018-04-02 07:22

  本文选题：聚集诱导发光材料　切入点：电聚合　出处：《华南师范大学学报(自然科学版)》2017年02期

【摘要】：以聚集诱导发光(AIE)材料咔唑基三苯乙烯衍生物(TPCz)为单体,采用循环伏安法(CV)原位聚合制备了咔唑基三苯乙烯衍生物多孔聚合物薄膜(TPCz-CMPs).利用红外光谱(FT-IR)、紫外-可见吸收光谱(UV-Vis)、高倍透射电镜(HR-TEM)等手段对其结构和形貌进行了表征,并对CMPs薄膜修饰的电极进行了循环优安(CV)、恒电流充放电(CP)及交流阻抗(EIS)等电化学性能测试.结果表明,TPCz-CMPs薄膜具有多孔结构,在电流密度为4A/g时,TPCz-CMPs薄膜电极的比电容达到193 F/g,是一种具有应用前景的超级电容器材料.
[Abstract]:The aggregate induced luminescence (AIEs) material, carbazolyl tristyrene derivative (TPCz), was used as monomer. The porous polymer films of carbazolyl tristyrene derivatives were prepared by in situ polymerization with cyclic voltammetry (CV). The structure and morphology of the films were characterized by FTIR, UV-Vis-Vis and HR-TEM. The electrochemical properties of the modified CMPs films were measured by cyclic amperometric charge / discharge (CMPs), constant current charge / discharge (CMPs) and electrochemical impedance spectroscopy (EIS). The results show that TPCz-CMPs thin films have porous structure. When the current density is 4A/g, the specific capacitance of TPCz-CMPs thin film electrode is 193F / g, which is a promising supercapacitor material.
【作者单位】： 华南师范大学化学与环境学院;
【基金】：国家自然科学基金项目(51203054) 博士后科学基金项目(2014M552192,2015T80906)
【分类号】：TB383.2;TM53

【相似文献】

相关期刊论文 前4条

1 王宇航;张秋禹;马明亮;尹常杰;寇晓康;;多孔聚合物微球成孔技术的最新研究进展[J];材料导报;2011年11期

2 陈忠元;居亚兰;张文锋;朱云峰;李李泉;;一种新型碱性多孔聚合物电解质的制备与性能研究[J];材料导报;2009年S1期

3 伍绍飞;喻桂朋;潘春跃;;有机纳米多孔聚合物(NOPs)概述[J];广州化工;2013年13期

4 ;[J];;年期

相关会议论文 前1条

1 李磊;;超临界二氧化碳发泡制备纳米多孔聚合物薄膜[A];2007年全国高分子学术论文报告会论文摘要集（上册）[C];2007年

相关硕士学位论文 前2条

1 刘献虎;基于Schiff碱反应的有机多孔聚合物的合成及应用[D];兰州大学;2013年

2 秦新新;模板法制备多孔聚合物材料及其吸附性能的研究[D];哈尔滨工业大学;2014年

，

本文编号：1699370