Ti对Al-Ti合金与金刚石的润湿性和把持力的影响

发布时间：2018-06-09 17:20

  本文选题：Al-Ti合金 + 金刚石　； 参考：《人工晶体学报》2017年10期

【摘要】：本文首先研究了Ti对Al-Ti合金与金刚石润湿性的影响,然后以不同Ti含量的Al-Ti合金为基体,加入金刚石,利用热压烧结制备没有和有金刚石铝基节块。测量了节块的抗弯强度并计算了铝基结合剂对金刚石的把持力。结果表明:随着Ti含量的增加,Al-Ti合金对金刚石的润湿性有明显的改善,所以当Ti含量为5wt%时,没有和含有金刚石的Al-Ti节块的抗弯强度值最高,分别为135 MPa和102.1 MPa;把持力系数最大,达到75.6%。
[Abstract]:In this paper, the effect of Ti on wettability of Al-Ti alloy and diamond was studied, then Al-Ti alloy with different Ti content was used as matrix, diamond was added into the matrix, and the aluminum matrix blocks without and with diamond were prepared by hot pressing sintering. The bending strength of the segment was measured and the holding force of aluminum based bond to diamond was calculated. The results show that the wettability of Al-Ti alloy is obviously improved with the increase of Ti content. Therefore, when Ti content is 5 wt%, the flexural strength of Al-Ti knots without and containing diamond is the highest. It was 135MPa and 102.1 MPA, respectively, and the holding force coefficient was the highest, reaching 75.6 MPA.
【作者单位】： 河南工业大学材料科学与工程学院;
【基金】：郑州市科技局自然科学项目(20150246)
【分类号】：TB34

【相似文献】

相关期刊论文 前10条

1 陈玉华;戈军委;黄春平;黄科辉;柯黎明;;搅拌摩擦加工原位合成Al-Ti颗粒增强铝基复合材料的微观结构[J];中国机械工程;2013年16期

2 谢正南;金刚石[J];中国建材;1985年03期

3 王松顺;超高压下掺杂烧结含硼金刚石多晶体的研究[J];科学通报;1984年02期

4 ARTHUR L.ROBinson;赵正保;;新颖材料——金刚石[J];新型碳材料;1987年02期

5 平木昭夫 ,川原田洋 ,王健男;金刚石状薄膜[J];新型碳材料;1988年02期

6 ;我国首次合成纳米级金刚石晶体薄膜[J];军民两用技术与产品;2001年01期

7 ;我国首次合成纳米级金刚石晶体薄膜[J];理化检验(物理分册);2001年03期

8 王光祖;苏联关于Mn—Ni—C系合金与金刚石晶体生长关系的研究[J];磨料磨具与磨削;1987年05期

9 ;我国首次合成纳米级金刚石晶体薄膜[J];新材料产业;2001年01期

10 王金斌,刘秋香,杨国伟,胡国彬,游建强;脉冲激光诱导液-固界面反应制备金刚石纳米晶[J];材料研究学报;1998年03期

相关重要报纸文章 前1条

1 何欣;金刚石芯片上的“实验室”[N];大众科技报;2002年

相关硕士学位论文 前2条

1 郑秋菊;同步辐射貌相术及金刚石晶体缺陷的貌相研究[D];燕山大学;2003年

2 魏娜然;新金刚石晶体结构及电子结构的第一性原理研究[D];大连理工大学;2006年

，

本文编号：2000520