绝缘子用球墨铸铁附件内部孔洞成因分析及改进措施

发布时间：2019-06-20 08:56

【摘要】：简述了绝缘子用球墨铸铁附件的重要性,对其缺陷的危害程度进行了说明,通过对球墨铸铁附件的解剖,针对解剖出的孔洞缺陷从原料、工艺、工装设备等方面进行了综合分析,得出孔洞缺陷是球墨铸铁附件壁厚变化显著和浇冒口设置不合理造成的,提出了改变浇冒口的形状数量及大小、控制浇注时铁液的温度,提高砂型的刚度的改进措施,消除了球墨铸铁附件的孔洞缺陷。
[Abstract]:The importance of nodular cast iron accessories for insulators is briefly described, and the harm degree of defects is explained. through the anatomy of nodular cast iron accessories, the comprehensive analysis of the dissected hole defects is carried out from the aspects of raw materials, technology, tooling equipment and so on. It is concluded that the hole defects are caused by the remarkable change of wall thickness of nodular cast iron accessories and the unreasonable setting of risers, and the number and size of castable risers are changed. The hole defects of nodular cast iron accessories are eliminated by controlling the temperature of molten iron and improving the stiffness of sand mold.
【作者单位】： 中电普瑞科技有限公司;
【分类号】：TM216

【相似文献】

相关期刊论文 前10条

1 林鹏;含裂纹与孔洞缺陷介质的脆性破坏行为[J];岩石力学与工程学报;2002年08期

2 唐艳丽;马春学;盛文斌;张春明;张勇;蒋振峰;韩庆吉;;水射法制备钢丸粒度及孔洞缺陷分布规律研究[J];山东理工大学学报(自然科学版);2010年01期

3 郑丽娟;周红梅;刘会莹;付宇明;;含埋藏孔洞缺陷金属构件电磁热止裂强化分析[J];中国机械工程;2012年11期

4 徐志辉;杜希刚;张守丰;麻硕;;HT250铸件表面孔洞缺陷分析[J];失效分析与预防;2011年04期

5 ;[J];;年期

6 ;[J];;年期

7 ;[J];;年期

8 ;[J];;年期

9 ;[J];;年期

10 ;[J];;年期

相关会议论文 前1条

1 陈伟;苏鹤洲;李金柱;;昆钢热轧板孔洞缺陷成因浅析[A];第八届全国连铸学术会议论文集[C];2007年

相关重要报纸文章 前1条

1 记者 杨礼兵邋特约记者 白方;孔洞检测仪察瑕疵于细微[N];湖北日报;2008年

相关硕士学位论文 前10条

1 徐华东;基于模态分析的红松方材内部孔洞缺陷检测[D];东北林业大学;2008年

2 于文勇;基于超声波原木内部孔洞缺陷定量检测[D];东北林业大学;2006年

3 张希栋;主要测试条件参数对原木孔洞缺陷应力波检测效果的影响[D];东北林业大学;2007年

4 宋世全;基于支持向量机的原木树种及原木内部孔洞缺陷辨识[D];东北林业大学;2012年

5 杨慧敏;基于能量法木材孔洞缺陷的超声定量检测研究[D];东北林业大学;2005年

6 黄涛;电镀工艺优化对铜金属层孔洞缺陷的影响[D];上海交通大学;2010年

7 吴鹏;优化铜种子层对电镀铜孔洞缺陷的改善[D];复旦大学;2011年

8 符正晴;基于PNN的板材孔洞缺陷红外热波检测及其识别技术[D];华东交通大学;2014年

9 孟宪静;基于模糊模式识别的木材孔洞缺陷识别模型的研究[D];东北林业大学;2014年

10 李文军;发动机曲轴铸造孔洞缺陷的分析[D];吉林大学;2013年

，

本文编号：2503096