真空二极管光电转换效率研究

发布时间：2018-01-04 14:56

  本文关键词：真空二极管光电转换效率研究　出处：《半导体光电》2017年02期 　论文类型：期刊论文

  更多相关文章： 光子增强型热电子发射 能量转换 真空二极管 NaCsSb

【摘要】：在光子增强型热电子发射转换机制的理论基础上,研究了NaCsSb真空二极管在光照和加热条件同时作用下的表现。光电转换效率实验测试了在不同波长以及不同温度条件下,NaCsSb真空二极管的电流-电压曲线和功率-电压曲线,并计算了NaCsSb真空二极管的光电转换效率。实验结果表明,光照和加热条件共同具备时,NaCsSb真空二极管产生的功率约为仅提供光照条件时的两倍多。在同一波长下,加热时的真空二极管转换效率更高。
[Abstract]:Based on the theory of photonic enhanced hot electron emission conversion mechanism. The performance of NaCsSb vacuum diode under both light and heating conditions was studied. The photoelectric conversion efficiency was measured at different wavelengths and at different temperatures. The current-voltage curves and power-voltage curves of NaCsSb vacuum diodes, and the photoelectric conversion efficiency of NaCsSb vacuum diodes are calculated. The power generated by NaCsSb vacuum diodes is more than twice as high as that of the vacuum diodes provided with only illumination conditions, and the conversion efficiency of the vacuum diodes heated at the same wavelength is higher than that of the vacuum diodes with the same wavelength.
【作者单位】： 南京理工大学电子工程与光电技术学院;
【基金】：国家自然科学基金项目(91433108)
【分类号】：TN111
【正文快照】： 0引言光热发电和光伏发电是比较成熟的太阳能发电技术。太阳能热发电主要通过对太阳光聚焦收集太阳热能,再通过热机转换发电。实用的太阳能光热发电系统的年净发电效率为12%~25%。太阳能光伏发电利用光电转化或光量子效应,通过光功能材料接收太阳辐射,将光能转化为电能。目前,

【相似文献】

相关期刊论文 前4条

1 王冠中,李鹏,马玉蓉,方容川;金属/PS/n-Si结构光电转换效率的研究[J];科学通报;1997年09期

2 陈旭涛;张秀霞;姜涛;李文锦;付小园;吴晓雨;彭静;;提高Nano-SiC薄膜的转化效率分析[J];科技创新与应用;2014年04期

3 胡南江;吕向菲;赵冉;马宏瑞;汤伟;马春林;;多孔金字塔型黑硅电极的制备及其光电性能研究[J];陕西科技大学学报(自然科学版);2013年05期

4 ;[J];;年期

相关重要报纸文章 前1条

1 记者 王正喜;2%,每年纯利增亿元![N];徐州日报;2010年

相关硕士学位论文 前1条

1 朱子菱;新型镉基半导体纳米结构的合成与光电性能研究[D];天津大学;2014年

，

本文编号：1378875