氯化钾镀锌溶液抗二价铁添加剂

发布时间：2017-12-28 17:08

  本文关键词：氯化钾镀锌溶液抗二价铁添加剂　出处：《电镀与环保》2016年01期 　论文类型：期刊论文

  更多相关文章： 二价铁 电流密度范围 镀锌层 镀层质量 镀件 三价铁 镀前处理 镀锌光亮剂 电镀工 除油

【摘要】：正氯化钾镀锌溶液中的铁是主要杂质之一。它以两种形式存在:一种是二价铁,另一种是三价铁。三价铁对镀液危害不大,容许质量浓度高,即使达到10g/L时镀液变得浑浊,仍能获得较正常的镀锌层。鉴于此,我们可以忽略三价铁的影响。另一种是二价铁,它不仅使电流密度范围明显缩小,还使镀层变得粗糙,尤其对高电流密度区镀层质量的影响较大。赫尔槽试验发现:当二价铁的质量浓度为
[Abstract]:Iron in the solution of positive potassium chloride zinc plating is one of the main impurities. It exists in two forms: one is two valence iron, the other is trivalent iron. The trivalent iron has little harm to the plating solution, allowing the mass concentration to be high. Even if the plating solution becomes turbid when it reaches 10g/L, it can still obtain a more normal zinc plating layer. In view of this, we can ignore the effect of trivalent iron. The other is two valent iron, which not only reduces the current density obviously, but also makes the coating become rough, especially on the quality of the high current density zone. The Hull trough test found that the mass concentration of two valence iron is
【作者单位】： 上海永生助剂厂;
【分类号】：TQ153
【正文快照】： 氯化钾镀锌溶液中的铁是主要杂质之一。它以浸碱液后不立刻进行电镀,而是将待镀件放置在空两种形式存在:一种是二价铁,另一种是三价铁。三气中,一般可放置1~2h。如需要电镀,再用自来价铁对镀液危害不大,容许质量浓度高,即使达到水清洗一下就可入槽。这样做的目的是让零件表面1

【相似文献】

相关期刊论文 前10条

1 宫珏;关于土壤中的二价铁[J];中国环境监测;1989年02期

2 张明婉;师明泽;孟宪级;;地热水中二价铁的现场快速测定[J];化学工业与工程;1990年Z1期

3 裴夫国;庄红;吕学举;李晨光;龚琼翔;刘静波;;多肽-铁制备及其性质研究[J];食品科学;2007年10期

4 华雁芬,刘莉;玻璃中亚铁和总铁的连续测定[J];玻璃与搪瓷;1991年05期

5 李圭白;;地下水除铁技术的若干新发展[J];建筑技术通讯(给水排水);1983年03期

6 锡环;;用二价铁复盐进行棉织物还原染色[J];国外丝绸;2004年06期

7 赵毅伟;;嗜酸性原核生物与二价铁矿物质作用机理及其对环境的影响[J];科协论坛(下半月);2012年10期

8 肖华;钟桂香;;枸橼酸铁胺糖浆配制方法商榷[J];中国药业;2008年24期

9 张丽霞;在pH2.5～7.0范围内,用Acidithiobacillus ferrooxidans细菌生物氧化二价铁[J];湿法冶金;2003年04期

10 王加柱;;低温镀铁用室温起镀法介绍[J];电镀与环保;1984年06期

相关重要报纸文章 前1条

1 健康时报特约记者 郑杨;补铁搭点维生素C[N];健康时报;2009年

相关硕士学位论文 前1条

1 蒋晓璇;不同方法产生硫酸根自由基降解双酚A的研究[D];复旦大学;2013年

，

本文编号：1346663