银色油滴釉的研制

发布时间：2018-01-06 17:16

本文关键词：银色油滴釉的研制　出处：《硅酸盐通报》2016年03期 　论文类型：期刊论文

【摘要】：以高岭土、方解石、烧滑石、石英、长石和Fe_2O_3、Co_3O_4为原料,制备出效果优良的银色油滴釉。研究了不同Fe_2O_3含量和Co_3O_4含量对油滴釉效果的影响,结果表明随着氧化铁含量的增加,油滴颜色逐渐向银色转变,但加入量过多则釉面会变得凸凹不平,质量变差,当Fe_2O_3加入量为0.0255 mol时,效果最好,适当的Co_3O_4不仅可以使油滴效果更加明显,并且使油滴的银色更加突出,当Co_3O_4加入量为2wt%时,油滴效果最好。通过研究烧成温度、施釉厚度等工艺条件对油滴釉效果的影响,得出了最佳的工艺条件为烧成温度1270℃,保温30 min,施釉厚度为1.2~1.5 mm。
[Abstract]:With kaolinite, calcite, quartz and feldspar, talc burning, Fe_2O_3, Co_3O_4 as raw materials, preparation of the excellent effect of silver oil drop glaze. The effects of different Fe_2O_3 content and Co_3O_4 content of oil drop glaze effect, the results show that with the increase of the content of ferric oxide, oil drops gradually to the silver color change, but added excessive glaze will become uneven, poor quality, when the amount of Fe_2O_3 was 0.0255 mol, the best, the appropriate Co_3O_4 can not only make the oil drop effect is more obvious, and the oil drop of silver is more prominent, when the Co_3O_4 content is 2wt%, the best oil firing temperature through effect. Study on effect of glaze thickness and other process conditions on the oil drop glaze effect, obtained the optimum technological conditions for firing temperature of 1270 DEG C, 30 min insulation, glaze thickness is 1.2~1.5 mm.

【作者单位】：景德镇陶瓷学院国家日用及建筑陶瓷工程技术研究中心;
【分类号】：TQ174.43
【正文快照】： 1引言我国黑釉瓷的生产历史悠久,可以追溯到汉朝,在其后的隋、唐代也有烧制,但在宋代,其生产规模进一步扩大,窑址遍布南北。宋朝盛行“斗茶”,而斗茶所用的茶具中茶盏是最重要的器皿之一,而黑釉茶盏因其底色较深,能较好的衬托出茶汤的颜色,且其良好保温性更有利于茶叶的香气逸

【相似文献】

中国期刊全文数据库前10条

1 秋;;金油滴釉[J];河北陶瓷;1993年02期

2 詹益州;;高温油滴釉的研制[J];佛山陶瓷;2013年03期

3 缪松兰,马光华,资文华;油滴釉制作工艺的研究[J];中国陶瓷工业;2002年02期

4 郭强;油滴釉的仿制实验[J];中国陶瓷;2000年05期

5 王金锋,刘伟杰,刘保华,李智涛;仿南宋油滴釉的研制[J];陶瓷工程;2001年06期

6 武同青;罗瑞征;;中温炻器天目油滴釉的研制及影响因素的探讨[J];陶瓷;2006年03期

7 武同青;罗瑞征;;中温炻器天目油滴釉的研制[J];陶瓷科学与艺术;2005年06期

8 温得有;油滴釉和兔毫釉的研制及其形成机理[J];山东陶瓷;1999年03期

9 武同青;罗瑞征;;中温炻器天目油滴釉的研制[J];陶瓷科学与艺术;2005年05期

10 王金锋,刘伟杰,刘保华,李智涛;仿南宋油滴釉的研制[J];陶瓷科学与艺术;2003年03期