石墨化无烟煤配入量对炭块性能的影响

发布时间：2018-03-14 16:04

  本文选题：电煅煤　切入点：石墨化煤　出处：《炭素技术》2017年04期 　论文类型：期刊论文

【摘要】：将石墨化无烟煤经破碎、筛分和磨粉处理后,按照不同比例配入炭块配料中,研究了石墨化无烟煤配入量对炭块性能的影响。结果表明,随着炭块试样中石墨化无烟煤配入量的增加,试样的体积密度提高、耐压强度降低、抗氧化性能改善。在多数情况下,加入石墨化无烟煤能提高试样的导热系数,降低试样的铁水熔蚀指数;石墨化无烟煤加入量在50%,且以颗粒的形式加入时,试样有最大导热系数,此时试样的抗铁水熔蚀性能也最好。加入石墨化无烟煤的试样,耐碱性全部为优。
[Abstract]:The effect of the amount of graphitized anthracite on the properties of carbon block was studied by mixing the graphitized anthracite into carbon block according to different proportions after crushing, screening and grinding. With the increase of the amount of graphitized anthracite in the carbon block, the bulk density of the sample is increased, the compressive strength is decreased, and the oxidation resistance is improved. In most cases, the thermal conductivity of the sample can be improved by adding graphitized anthracite. Reducing the molten iron corrosion index of the sample; when the amount of graphitized anthracite is 50%, and when the sample is added in the form of particles, the sample has the maximum thermal conductivity, and the sample has the best corrosion resistance to molten iron. The sample with graphitized anthracite is added. Alkali resistance is excellent.
【作者单位】： 中冶南方邯郸武彭炉衬新材料有限公司;
【分类号】：TQ127.11

【相似文献】

相关期刊论文 前10条

1 景立圯;;高应变石墨的研究[J];炭素技术;1990年03期

2 陈振山;碳石墨材料的耐腐蚀性能[J];电碳技术;1981年01期

3 邱海鹏,郭全贵,宋永忠,翟更太,宋进仁,刘朗;石墨材料导热性能与微晶参数关系的研究[J];新型炭材料;2002年01期

4 叶麟;石墨化升温曲线的研究[J];炭素;2005年02期

5 邓念;袁观明;别望望;董志军;张贵萍;赵杰;李轩科;;细粒石墨材料的热压制备[J];武汉科技大学学报;2010年04期

6 解胜利;浸渍对炭-石墨材料孔隙孔径的影响[J];炭素技术;2000年03期

7 徐迎节;;超低灰无烟煤石墨化产品的生产及应用[J];煤炭加工与综合利用;2013年03期

8 杜林虎,陈大明,潘伟,陈健;超声波对鳞片状石墨的粉碎作用及结构影响[J];硅酸盐通报;2000年04期

9 M.Kakuta;晨雨;;煅后焦性质和以它们为骨料制备的石墨化棒性质之间的关系[J];炭素技术;1986年04期

10 ;超高强石墨材料[J];中国搪瓷;1998年05期

相关会议论文 前1条

1 李明宇;李平;张启彪;鲍彬;;我国光伏发电与硅晶体生长用等静压石墨[A];第22届炭—石墨材料学术会论文集[C];2010年

相关硕士学位论文 前1条

1 史学敏;连续式石墨化电炉冷却系统的优化设计及数值模拟[D];东北大学;2011年

，

本文编号：1611928