发布时间：2018-03-18 12:38

  本文选题：季铵化壳聚糖　切入点：纤维素　出处：《现代化工》2017年08期 　论文类型：期刊论文

【摘要】：以季铵化壳聚糖(QCS)、纤维素(CM)和小分子游离胍(Guanidine)为原料,戊二醛(GA)为交联剂,采用化学交联法制备了具有全互穿网络结构的QCS-CM-Guanidine阴离子交换膜,并对其耐碱性、含水率、溶胀度、机械强度以及电导率等相关性能进行测定。结果表明,CM和Guanidine的引入,对膜的机械强度和导电性能有所增强,将QCS-CM40%-Guanidine2.5%膜在4mol/L的KOH浓溶液中浸渍96 h,膜的电导率损失量仅为4%,离子交换量的损失量为7%,表明该膜具有良好的耐碱稳定性。
[Abstract]:QCS-CM-Guanidine anion exchange membranes with full interpenetrating network structure were prepared by chemical crosslinking with quaternary ammonium chitosan (QCS-CM-Guanidine) and small molecular free guanidine (guanidine) as raw materials and glutaraldehyde (Glutaraldehyde) as crosslinker. The mechanical strength and electrical conductivity were measured. The results showed that the mechanical strength and electrical conductivity of the film were enhanced with the introduction of CM and Guanidine. When the QCS-CM40- Guanidine 2.5% membrane was impregnated in 4mol / L KOH solution for 96 h, the loss of conductivity was only 4%, and the loss of ion exchange was 7%, which indicated that the membrane had good alkali-resistant stability.
【作者单位】： 辽宁石油化工大学化学化工与环境学部石油化工学院;
【基金】：辽宁省科技厅博士启动项目(20141126) 辽宁省教育厅科学研究一般项目(L2013153) 辽宁石油化工大学博士启动基金(2013XJJ-006)
【分类号】：TM911.4;TQ425.236

【参考文献】

相关期刊论文 前6条

1 陈荣;李昂;房世超;毕慧平;胡朝霞;陈守文;;自交联型季铵化聚醚砜阴离子交换膜的制备与性能[J];高分子学报;2016年04期

2 倪红军;裴一;张庆廷;赵敬;汪兴兴;黄明宇;;SPEEK/PANI/PWA复合质子交换膜的制备及性能[J];现代化工;2015年11期

3 杨贵涵;潘远凤;张家佳;;功能化低聚物胍盐阳离子单体材料合成与表征[J];化工新型材料;2015年02期

4 于汇波;姜俊舟;王吉林;王璐璐;封瑞江;;季铵化壳聚糖掺杂荷正电聚苯乙烯微球复合膜的制备及去除Cr~(6+)研究[J];石化技术与应用;2013年04期

5 刘玲玲;丁蕾;徐莉;乔锦丽;盛嘉伟;;化学交联聚乙烯醇改性纤维素碱性阴离子交换复合膜的制备与性能[J];物理化学学报;2011年11期

6 姚秀清;杨翔华;;稀盐酸预处理木质纤维素研究[J];辽宁石油化工大学学报;2010年04期

相关博士学位论文 前1条

1 戴磊;TEMPO氧化法纳米纤维素及其复合膜的制备和性能研究[D];江南大学;2015年

相关硕士学位论文 前1条

1 崔玉芳;全钒液流电池用新型胍类阴离子交换膜的研究[D];北京化工大学;2012年

【共引文献】

相关期刊论文 前10条

1 邸慧双;崔s，

本文编号：1629613