有机玻璃粘接缝抗拉强度的Weibull统计分析

发布时间：2018-04-09 14:47

  本文选题：有机玻璃　切入点：粘接缝　出处：《硅酸盐通报》2017年04期

【摘要】：测试了由四种粘接工艺(常规粘接、快料粘接、常温紫外光固化粘接和升温紫外光固化粘接)制备的有机玻璃粘接缝试样的抗拉强度;应用Weibull分布理论分析了四组试样抗拉强度数据的分散性。研究表明:Weibull分布函数能够很好地描述有机玻璃粘接缝的强度分布;快料粘接工艺制备的粘接缝试样平均强度较高,粘接系数为0.83,且粘接过程耗时短,较适用于大型工程中有机玻璃结构的拼接。
[Abstract]:The tensile strength of an organic glass bonded joint prepared by four bonding processes ( conventional bonding , fast adhesive bonding , normal temperature ultraviolet curing adhesion and temperature rise ultraviolet curing adhesion ) was tested . The Weibull distribution theory was applied to analyze the dispersion of the tensile strength data of the four groups of specimens . The results show that the Weibull distribution function can describe the strength distribution of the bond joint of the PMMA . The results show that the average strength of the adhesive joint sample prepared by the fast material bonding process is higher , the bonding coefficient is 0.83 , and the bonding process is short time , and is suitable for splicing of the organic glass structure in large engineering .

【作者单位】： 浙江大学化工机械研究所;中国科学院高能物理研究所;
【基金】：中国科学院战略性先导科技专项(A类)项目(XDA10010200)
【分类号】：TQ171.68

【相似文献】

相关期刊论文 前5条

1 金宗哲,马眷荣,汪林生;结构陶瓷弯曲强度的Weibull统计实验研究[J];硅酸盐学报;1990年02期

2 白世鸿,陈彦,乔生儒,陈玉顺,康沫狂;SiC陶瓷高温弯曲强度的Weibull模量研究[J];机械强度;2000年04期

3 王恒武,王继辉,黄再满,朱京杨;用Weibull评价表面处理对玻璃纤维强度影响[J];武汉理工大学学报;2003年06期

4 许崇海,艾兴,黄传真,刘健;Weibull模数与陶瓷刀具可靠性[J];济南大学学报(综合版);1997年02期

5 ;[J];;年期

相关硕士学位论文 前1条

1 傅滟;等静压成型99氧化铝陶瓷及其抗折强度的Weibull分析[D];济南大学;2014年

，

本文编号：1726879