氯化钡和聚乙烯醇复掺改性石膏正交试验研究

发布时间：2018-04-21 02:16

  本文选题：建筑石膏 + 复合胶凝材料　； 参考：《硅酸盐通报》2017年09期

【摘要】：采用正交试验研究了氯化钡和聚乙烯醇(PVA)复掺改性石膏复合胶凝材料的力学性能、吸水率和耐水性,并分析了改性机理。研究发现,氯化钡掺量为15%,水胶比为0.53,PVA掺量为3%时,石膏基复合胶凝材料28 d抗折软化系数最高;水胶比为0.53,氯化钡掺量为20%,PVA掺量为2%时,石膏基复合胶凝材料28 d抗压软化系数最高。通过XRD和SEM分析发现:复掺改性剂可以改变其微观形貌、减少孔隙率、使晶体结构变得密实。
[Abstract]:The mechanical properties, water absorption and water resistance of barium chloride and polyvinyl alcohol polyvinyl alcohol (PVA) modified gypsum composite cementitious materials were studied by orthogonal test, and the modification mechanism was analyzed. It is found that when the content of barium chloride is 15 and the ratio of water to binder is 0.53 and the ratio of water to binder is 0.53, and the ratio of water to binder is 0.53, the ratio of water to binder is 0.53, and the ratio of water to binder is 0.33 and the ratio of water to binder is 0.33 to PVA, The pressure softening coefficient of gypsum based composite cementitious material was the highest in 28 days. By XRD and SEM analysis, it was found that the mixed modifier could change the microstructure, reduce the porosity and make the crystal structure dense.
【作者单位】： 长安大学材料科学与工程学院;陕西铁路工程职业技术学院;
【基金】：陕西省自然科学基础研究计划(2017JM5146) 新疆兵团工业科技攻关项目(2014BA017);新疆兵团科技支疆计划项目(2014AB027)
【分类号】：TQ177.3

【相似文献】

相关期刊论文 前10条

1 吕斌如,毛友红,孙爱平,贺才勇;液体氯化钡工业化生产及应用[J];氯碱工业;2001年07期

2 陈英军;含钡废渣制氯化钡的研究[J];无机盐工业;2001年05期

3 温占玺;;氯化钡与硫氢化钠的制法[J];化工之友;2001年05期

4 冯福奎;氯化钡[J];化学世界;1954年04期

5 骆功权;硫酸淡化氯化钡废渣[J];劳动保护;1980年09期

6 陈其熵;;提高氯化钡产、质量的探索[J];无机盐工业;1980年05期

7 高永华;;硫酸淡化氯化钡废渣[J];无机盐工业;1981年01期

8 朱法寿;;氯化钡简易生产法[J];无机盐工业;1984年03期

9 寇丽华;中国在美国倾销氯化钡[J];无机盐工业;1985年05期

10 逄先敏,陈允安;关于氯化钡产品中硫、铁的研究[J];无机盐工业;1985年08期

相关会议论文 前1条

1 王会昌;李东霞;郝毅军;;5000t/a液体氯化钡的工业化生产[A];2008年中国镁盐行业年会暨节能减排新技术推介会专辑[C];2008年

相关重要报纸文章 前5条

1 贾占水;氯化钡：升级换代成主攻方向[N];中国化工报;2006年

2 通讯员 汪玲;旬阳年产2万吨氯化钡项目开工建设[N];安康日报;2008年

3 曹萍;氯化钡采购保总成本最低[N];中国石化报;2011年

4 郑传明　本报记者 柯士雨 实习生 王远白;产业链条再延伸 年增产值三千万[N];贵阳日报;2009年

5 罗元超;梳理原辅材料检验标准[N];中国石化报;2011年

，

本文编号：1780492