发泡水泥性能的计算关系式总结

发布时间：2018-04-27 00:17

  本文选题：发泡水泥 + 抗压强度　； 参考：《新型建筑材料》2017年07期

【摘要】：由于发泡水泥的密度不同,强度及导热系数也随之发生变化;生产发泡水泥产品的水温要根据环境温度、水泥温度进行调节,经过大量试验和理论研究得出发泡水泥的密度与强度的计算关系式P_x=(ρ/ρ_f)~2·P·N·K、生产发泡水泥的水温计算公式W=90Y-2Wc、导热系数计算公式λ=((λ_2-λ_1)ρ_1)/([y·ρ_2-(y-1)ρ_1]Z)+λ_1。
[Abstract]:Because of the different density of foamed cement, the strength and thermal conductivity also change. The water temperature of producing foamed cement products should be adjusted according to the environment temperature and cement temperature. After a large number of experiments and theoretical studies, the formula for calculating the density and strength of foamed cement is obtained, which is the formula for calculating the water temperature of the foamed cement produced by 蟻 / 蟻 ffjiao 2 P N K, the formula for calculating the water temperature of the foamed cement W90Y-2Wc, and the formula for calculating the thermal conductivity of the cement, 位 (位 _ 2- 位 _ 1) 蟻 1 / ([y 蟻 _ 2-y ~ (-1) 蟻 _ 1] Z) 位 _ (1).
【作者单位】： 江西省科学院应用化学研究所;广州轻能化工建材机械科技公司;
【分类号】：TQ172.1

【相似文献】

相关期刊论文 前10条

1 张延飞;;发泡水泥新材料研究探讨[J];科技风;2010年09期

2 张磊蕾;王武祥;廖礼平;王爱军;;用硫铝水泥制备发泡水泥的试验研究[J];新型建筑材料;2013年12期

3 佘海龙;耿春雷;王冬;;无机化学发泡水泥技术研究进展[J];商品混凝土;2012年07期

4 孙诗兵;陈华;兰明章;牛寅平;田英良;;聚合物对发泡水泥制品孔结构和性能影响[J];北京工业大学学报;2014年06期

5 刘品华,李文;轻质发泡水泥制品技术[J];企业技术开发;1998年07期

6 杜传伟;李国忠;;新型发泡水泥材料的研究制备[J];建筑砌块与砌块建筑;2013年02期

7 兰明章;王清;陈智丰;刘成健;;超轻普通发泡水泥保温板的制备试验研究[J];硅酸盐通报;2014年08期

8 黄阳;张文信;;发泡水泥隔墙板简易切割机的设计[J];机电产品开发与创新;2013年01期

9 侯彦叶;李冬梅;;我国发泡水泥保温板的研究现状[J];四川化工;2014年02期

10 苏秀霞;曹鹏妮;郑小鹏;;白泥纤维对发泡水泥性能影响的研究[J];陕西科技大学学报(自然科学版);2014年03期

相关会议论文 前2条

1 张磊蕾;王武祥;廖礼平;王爱军;;用硫O端�泥制备发泡水泥的试验研究[A];2013年混凝土与水泥制品学术讨论会论文集[C];2013年

2 张磊蕾;王武祥;宋晓辉;廖礼平;王爱军;;用普硅水泥制备发泡水泥的试验研究[A];2013年混凝土与水泥制品学术讨论会论文集[C];2013年

相关重要报纸文章 前1条

1 记者 魏国林;超级水泥发泡剂“泡皇”隆重面市[N];中国建材报;2007年

相关硕士学位论文 前3条

1 曹鹏妮;白泥纤维/陶粒增强发泡水泥的制备和性能研究[D];陕西科技大学;2015年

2 代丹丹;超轻发泡水泥保温板孔结构与性能关系的研究[D];北京工业大学;2016年

3 杨婷松;发泡水泥的制备工艺及理化性能研究[D];济南大学;2013年

，

本文编号：1808331