玄武岩纤维混凝土早期裂缝试验研究

发布时间：2018-04-27 17:00

  本文选题：玄武岩纤维混凝土 + 早期收缩裂缝　； 参考：《硅酸盐通报》2017年11期

【摘要】：为了研究玄武岩纤维混凝土早期开裂性能,对不同长度纤维和不同体积掺量的玄武岩纤维混凝土进行试验,结果显示:玄武岩纤维混凝土相对于普通混凝土裂缝降低明显,玄武岩纤维混凝土早期收缩裂缝随纤维长度增加先减小后缓慢增加,最佳阻裂纤维长度为18 mm,早期收缩可见裂缝随纤维体积掺量的增加而减小,当体积掺量到0.2%时可见裂缝基本消失。随着混凝土强度提高纤维混凝土的抗裂指标逐渐降低,裂缝更加短小。
[Abstract]:In order to study the early cracking performance of basalt fiber concrete, the experimental results of basalt fiber reinforced concrete with different length and volume content show that the crack of basalt fiber reinforced concrete is obviously lower than that of ordinary concrete. The early shrinkage crack of basalt fiber reinforced concrete decreases first and then increases slowly with the increase of fiber length. The optimum crack length is 18 mm, and the early shrinkage crack decreases with the increase of fiber volume. When the volume is up to 0.2, the crack can be seen to disappear. With the increase of concrete strength, the crack resistance index of fiber reinforced concrete decreases gradually, and the crack becomes shorter.
【作者单位】： 湖南城市学院;长沙理工大学;
【基金】：国家重点研究发展计划(973计划)(2015CB057700) 国家级大学生创新项目(201611527001)
【分类号】：TU528.572

【相似文献】

相关期刊论文 前10条

1 李国栋;王宗林;;间歇浇筑板式混凝土的早期约束收缩效应分析[J];工业建筑;2014年04期

2 刘仍光;王力尚;周康;杨建伟;李晶;阎培渝;;燥热环境中混凝土早期开裂的改善措施研究[J];硅酸盐通报;2013年04期

3 郭丹;;材料软设计理论在混凝土中的应用初探[J];江西建材;2014年12期

4 黄严芬;;预拌混凝土早期开裂的控制[J];价值工程;2011年16期

5 嵇仙宝;;海相状态下混凝土腐蚀机理及防腐措施研究[J];施工技术;2011年S1期

6 高原;张君;韩宇栋;;基于环约束试验的混凝土早期开裂行为评价[J];建筑材料学报;2012年05期

7 王玉瑛;王丽霞;王晔;李达;;浅谈预拌混凝土需要什么样的水泥[J];商品混凝土;2014年05期

8 马新伟;李学英;朱卫中;钮长仁;;部分约束条件下中低水灰比混凝土开裂的预测[J];建筑材料学报;2006年05期

9 王冲;张洪波;杨长辉;钱觉时;钟明全;李豪举;;水泥细度对水泥水化及混凝土早期开裂影响[J];建筑材料学报;2013年05期

10 王力尚;刘仍光;李晶;杨建伟;周康;阎培渝;;SAP对燥热环境中混凝土早期开裂的改善作用[J];混凝土;2014年02期

相关会议论文 前1条

1 吴雄;杨文;王军;赵日煦;王发洲;;自养护混凝土中水分传输机制模型的研究[A];2011年混凝土与水泥制品学术讨论会论文集[C];2011年

，

本文编号：1811556