提高合金钢镀银高温结合力的工艺研究

发布时间：2018-05-19 16:05

  本文选题：合金钢 + 电镀银　； 参考：《电镀与涂饰》2017年15期

【摘要】：研究了影响合金钢镀银产品高温结合力的因素,从打底层选择、前处理活化效果、返工产品底镀层褪除状态、产品尺寸等方面进行试验。结果表明:采用低应力的氨基磺酸盐镀镍取代传统全氯化物预镀镍打底后,合金钢镀银的高温结合力大大提升,且几乎不受产品尺寸的影响。前处理活化液中杂质铜离子的积累和返工产品底镀层褪除的彻底程度对合金钢镀银高温结合力有较大影响。
[Abstract]:The factors that affect the high - temperature bonding force of alloy steel silvering products are studied . The results show that the high - temperature bonding force of the alloy steel is greatly improved from the bottom layer selection , the pretreatment activation effect , the bottom plating condition of the rework product , the product size and so on . The results show that the high - temperature bonding force of the alloy steel silver plating is greatly improved after the traditional full - chloride pre - plating nickel plating is replaced by the low - stress aminosulfonate nickel plating , and the total amount of impurity copper ions in the pretreatment activating solution has a great influence on the high - temperature bonding force of the alloy steel plated silver .
【作者单位】： 河南航天精工制造有限公司;
【分类号】：TG174.44;TQ153.16

【相似文献】

相关期刊论文 前10条

1 李明;;氨基磺酸盐镀铁工艺的研究[J];表面技术;1990年06期

2 李明;;氨基磺酸盐镀铁工艺的研究[J];电镀与环保;1990年06期

3 吴水清;;氨基磺酸盐在电镀工业中的应用[J];表面技术;1991年04期

4 俞寅辉;乔敏;高南箫;冉千平;刘加平;;苯酚类衍生物对氨基磺酸盐系减水剂分散性能的影响[J];绿色建筑;2013年02期

5 张海燕,曾良宇;氨基磺酸盐阳极分解历程探讨[J];材料保护;1985年05期

6 阎培渝;王悦;;可溶碱对水泥/氨基磺酸盐减水剂相容性的影响[J];建筑材料学报;2006年05期

7 王俊达;李远;;氨基磺酸盐系与萘系减水剂复配的应用研究[J];辽宁建材;2011年03期

8 田峰;姬清华;;氨基磺酸盐镀镍的微观织构与硬度[J];电镀与环保;2012年04期

9 朱珍芳;;氨基磺酸盐减水剂在C50泵送混凝土中的应用[J];山西建筑;2006年13期

10 李文薇;李诚;裴梅山;;新型氨基磺酸盐类超塑化剂的合成[J];济南大学学报(自然科学版);2006年01期

相关会议论文 前1条

1 丁寅;刘加平;缪昌文;温勇;周伟玲;;掺氨基磺酸盐泵送剂水泥浆体的增强、保坍微观机理研究[A];《硅酸盐学报》创刊50周年暨中国硅酸盐学会2007年学术年会论文摘要集[C];2007年

，

本文编号：1910729