酚醛树脂对高软化点沥青的发泡行为及生物挂膜性能的影响

发布时间：2018-05-29 10:30

  本文选题：泡沫炭 + 酚醛树脂　； 参考：《华东理工大学学报(自然科学版)》2017年04期

【摘要】：以高软化点沥青为原料,采用自发泡法制备泡沫炭,将其用作生物污水处理固菌载体材料,并通过添加适量的酚醛树脂以提高泡沫炭的开孔率,进而提高其生物挂膜量。研究结果表明:当在高软化点沥青中添加酚醛树脂的质量分数为30%时,所制泡沫炭的开孔率高达100%,生物挂膜量(质量分数)达5.4%;当酚醛树脂的添加质量分数为40%时,所制泡沫炭的压缩强度达5.2MPa,但其开孔率较低,孔结构的均一性较差。
[Abstract]:Foamed carbon was prepared from asphalt with high softening point by spontaneous bubble method. It was used as the carrier material for biological wastewater treatment. By adding appropriate amount of phenolic resin, the open porosity of foamed carbon was increased and the amount of biofilm was increased. The results show that when the mass fraction of phenolic resin is 30, the porosity of foamed carbon is up to 100, and the amount of biofilm (mass fraction) reaches 5.4%, and when the added mass fraction of phenolic resin is 40? The compressive strength of the foamed carbon is 5.2 MPA, but the porosity is low and the homogeneity of pore structure is poor.
【作者单位】： 华东理工大学化学工程国家重点实验室上海市多相结构材料化学工程重点实验室特种功能高分子材料及相关技术教育部重点实验室;
【基金】：国家自然科学基金(51472086,51002051) 上海市自然科学基金(12ZR1407200)
【分类号】：TB383.4;TQ127.11

【相似文献】

相关期刊论文 前10条

1 吴锡琪;;用气体激光自动测定玻璃的软化点[J];玻璃;1979年02期

2 ;科技简讯[J];林化科技通讯;1982年02期

3 ;以α—蒎烯为原料的高软化点聚萜烯(中试)通过鉴定[J];广东化工;1982年01期

4 伍宏标;玻璃软化点温度的计算方法[J];玻璃;1988年01期

5 Т.Л.Молокова;由宝娣;;高软化点沥青基炭制品焙烧的研究[J];炭素技术;1983年05期

6 霍华林;;缩短沥青熬制周期[J];氯碱工业;1982年06期

7 刘光彬;用玻璃物性配合化学分析控制成分和密度变化[J];玻璃;1992年03期

8 吕景文,郭国栋;L~2MCP可溶芯玻璃的研究[J];长春光学精密机械学院学报;1989年01期

9 伍洪标;玻璃软化点温度的简易计算方法[J];玻璃与搪瓷;2004年04期

10 丁时炳;;关于炭素制品生产用沥青[J];炭素技术;1983年04期

，

本文编号：1950545