沉淀法白炭黑的分散性
本文选题：白炭黑 + 湿法研磨 ； 参考：《华东理工大学学报(自然科学版)》2017年01期
【摘要】：提高白炭黑在轮胎橡胶中的分散性,有利于提高轮胎橡胶拉伸强度并降低其滚动阻力。本文利用高速湿法研磨,通过正交试验研究了研磨过程工艺参数对白炭黑分散性能的影响。结果表明锆球直径对白炭黑的分散性影响最大,在转速5 000r/min,分散时间80 min,锆球直径0.9mm,白炭黑质量20g,六偏磷酸钠(SHMP)质量分数2%的条件下白炭黑分散最佳,中位径(D50)可降至112nm。
[Abstract]:Increasing the dispersity of silica in tire rubber can improve the tensile strength of tire rubber and reduce its rolling resistance. In this paper, the effects of grinding process parameters on the dispersion properties of silica were studied by orthogonal experiment with high speed wet grinding. The results showed that the diameter of zirconium ball had the greatest influence on the dispersity of silica. Under the conditions of rotational speed 5 000 r / min, dispersing time 80 min, zirconium ball diameter 0.9 mm, white carbon black 20 g and sodium hexametaphosphate (SHMP) 2%, the dispersion of silica was the best, and the median diameter (D50) could be reduced to 112 nm.
【作者单位】： 华东理工大学材料科学与工程学院超细材料制备与应用教育部重点实验室;
【基金】：国家自然科学基金(91534202,91534122) 上海市基础重点研究项目(15JC1401300) 国家国际科技合作专项项目(2015DFA51220)
【分类号】：TQ127.2
【参考文献】
相关期刊论文 前9条
1 燕鹏华;梁滔;;白炭黑改性及其在橡胶中的应用研究进展[J];橡胶科技;2015年10期
2 张立;王礼;王廷山;戴圣佳;刘振锋;;白炭黑及其分散剂的发展及在轮胎中的应用[J];橡胶工业;2015年09期
3 陈婉婷;丁浩;曹丽;罗琴;崔程琳;;机械研磨对水介质中白炭黑颗粒解聚和分散的影响[J];中国粉体技术;2015年03期
4 景允伸;许宏;常华;张香兰;;成核阶段对沉淀法白炭黑团聚程度的影响[J];山东化工;2015年09期
5 曹丽;崔程琳;陈婉婷;丁浩;;沉淀法白炭黑颗粒在水介质中的解聚与分散研究[J];非金属矿;2014年06期
6 辛晓晶;;白炭黑在轮胎中的应用及其研究进展[J];广东化工;2012年11期
7 郑丽华;刘钦甫;程宏飞;;白炭黑表面改性研究现状[J];中国非金属矿工业导刊;2008年01期
8 张庆军,莫文玲,王占乐;沉淀法制备纳米白炭黑的结构及性质的研究[J];硅酸盐通报;2005年04期
9 王军民,王夏冰;球磨过程中粉末的行为变化[J];甘肃工业大学学报;1999年01期
【共引文献】
相关期刊论文 前10条
1 陈鹏宇;周梅芳;姜海波;李春忠;;沉淀法白炭黑的分散性[J];华东理工大学学报(自然科学版);2017年01期
2 薛兵;杨保俊;王百年;葛礼响;王仲汉;;氟硅酸废水制备白炭黑的改性研究[J];化工新型材料;2017年02期
3 席e，
本文编号：2073281
本文链接：https://www.wllwen.com/kejilunwen/huagong/2073281.html