聚羧酸系酯醚复配减水剂母液的制备及对水泥水化过程的影响

发布时间：2018-06-30 01:02

  本文选题：聚羧酸 + 减水剂　； 参考：《化学研究与应用》2017年12期

【摘要】：通过相互复渗技术将自制的聚酯型(PCS-1)和聚醚型(PCS-2)两类减水剂母液复配,系统地研究了两组分掺量变化对其性能的影响。利用傅立叶变换红外光谱仪(FTIR)、X射线衍射(XRD)、热重(TG-DTG)和比表面(BET)研究了加入复配母液的硬化水泥石微观结构。结果表明,复配母液减水剂的加入促进了水泥水化,减小了水泥石的比表面积、孔容和孔径。
[Abstract]:The self-made polyether type (PCS-1) and polyether type (PCS-2) two type water reducer was mixed with each other, and the effects of the two components on the properties of the two type water reducing agent were systematically studied. The hardened cement stones added to the compound mother liquid were studied by using the Fu Liye transform infrared spectrometer (FTIR), X ray diffraction (XRD), thermogravimetric (TG-DTG) and specific surface (BET). The results showed that the addition of water reducing agent of compound mother liquor promoted the hydration of cement and reduced the specific surface area of cement paste, Kong Rong and pore size.
【作者单位】： 河套学院农学系;内蒙古大学化学化工学院;河套学院理学系;
【基金】：内蒙古自治区高等学校科学研究项目(NJZY16337)资助 河套学院科学技术研究青年项目(HYZQ201411)资助
【分类号】：TQ172.1

【相似文献】

相关期刊论文 前8条

1 龚英;段国荣;黄国泓;;新型聚羧酸系保塑剂的性能研究[J];新型建筑材料;2010年11期

2 赵宝龙;;聚羧酸高性能外加剂(聚羧酸系减水剂)在客运专线工程中的应用[J];中国新技术新产品;2011年04期

3 毕化泗;孙延庆;汤乐丰;李柱;;砂对应用聚羧酸的商品混凝土的性能影响[J];广东建材;2012年09期

4 廖国胜;何正恋;刘佩;;新型聚羧酸系保坍剂的合成与性能研究[J];建材世界;2013年04期

5 廖秋林;郎春林;廖声金;;改性醚类聚羧酸超塑化剂的制备及性能研究[J];商品混凝土;2012年07期

6 邵强;雷翅;;一种高适应性聚羧酸保坍剂的制备及性能研究[J];广州建筑;2014年02期

7 郭鑫祺;;环保交联型聚羧酸专用保坍剂的合成与性能研究[J];新型建筑材料;2013年05期

8 陈军超;蔡其全;李萍;陈军磊;;聚羧酸系高性能混凝土外加剂的应用[J];中国高新技术企业;2012年13期

相关会议论文 前2条

1 陈国新;祝烨然;沈燕平;黄国泓;;聚羧酸系保坍剂的一步法合成及性能[A];中国建筑材料联合会混凝土外加剂分会第十四次会员代表大会--“科隆杯”混凝土外加剂论文集（上册）[C];2014年

2 林荣峰;常青山;王敏;付鹏;刘振华;;具有多种官能团聚羧酸高效减水剂的研制[A];中国建筑材料联合会混凝土外加剂分会第十四次会员代表大会--“科隆杯”混凝土外加剂论文集（上册）[C];2014年

相关硕士学位论文 前2条

1 肖煜;聚羧酸系高性能保坍剂的研究[D];武汉科技大学;2013年

2 毛玉成;聚羧酸大分子的合成及其在模具石膏中的应用[D];江南大学;2014年

，

本文编号：2084157