【摘要】：通过溶胶-凝胶法制备了锌-钆抗菌白炭黑。通过添加表面活性剂对材料进行改性,并探究了材料改性前后的粒径、比表面积和抗菌性能变化。采用粒度分析、BET、SEM和EDS等手段对样品进行表征。结果表明改性后材料的粒径减小,粒度分布相对集中,比表面积增大至275.20209 m~2/g。并对材料进行抗菌性能检测,结果表明改性后材料的抗菌性能有一定的增强,锌-钆抗菌白炭黑的杀菌率可达90.29%。
[Abstract]:The zinc gadolinium antibacterial white carbon black was prepared by the sol-gel method. The material was modified by adding surfactants, and the particle size, specific surface area and the change of antibacterial properties before and after the modification were investigated. The particle size analysis, BET, SEM and EDS were used to characterize the samples. The results showed that the particle size of the modified material was reduced and the particle size distribution phase was reduced. The specific surface area of the material was increased to 275.20209 m~2/g. and the antibacterial properties of the material were detected. The results showed that the antibacterial properties of the modified materials were enhanced, and the bactericidal rate of zinc gadolinium antibacterial white carbon black could reach 90.29%..
【作者单位】： 昆明理工大学理学院;昆明理工大学化学工程学院;
【基金】：国家自然科学基金(21677010) 昆明理工大学分析测试基金(2016T20110234)
【分类号】：TQ127.2

【相似文献】

相关期刊论文 前10条

1 陆春华,倪亚茹,许仲梓,张其土;无机抗菌材料及其抗菌机理[J];南京工业大学学报(自然科学版);2003年01期

2 王芬,朱建峰;无机抗菌材料的应用与研究展望[J];陶瓷工程;2001年05期

3 葛伟青;苑少强;郝斌;;无机抗菌材料的应用及其抗菌性能测试和评价[J];陶瓷;2007年07期

4 王旭;陆洪彬;吕剑强;陈忠凯;;新型无机抗菌材料的研制[J];常熟理工学院学报;2008年02期

5 张彬;付亮;唐晓宁;王晓楠;王梦颖;高国成;;载银无机抗菌材料的干燥及性能表征[J];硅酸盐通报;2013年02期

6 姚爱华,李殿超,杨殿范;无机抗菌材料及应用[J];世界地质;2001年02期

7 ;无机抗菌材料可杀SARS[J];化工进展;2003年11期

8 梁金生,梁广川,祁洪飞,冀志江,金宗哲,吴子钊;稀土复合磷酸盐无机抗菌材料对陶瓷活化水性能的影响[J];中国稀土学报;2003年02期

9 ;日产银系无机抗菌材料可杀SARS病毒[J];化工新型材料;2003年11期

10 李欢;张彬;唐晓宁;杨淑钊;姜鹏;王晓楠;;铜-镨抗菌白炭黑的制备与研究[J];化工新型材料;2013年12期

相关会议论文 前1条

1 王静;金宗哲;冀志江;梁金生;杨晓平;颜学武;;电气石基无机抗菌材料的研究[A];2002年材料科学与工程新进展（上）——2002年中国材料研讨会论文集[C];2002年

相关硕士学位论文 前1条

1 张定;稀土—银型抗菌白炭黑的制备及应用研究[D];昆明理工大学;2015年

，

本文编号：2141765