2507双相不锈钢钾盐蒸发罐腐蚀的原因分析

发布时间：2018-08-26 16:32

【摘要】：以某院设计的两个项目中的蒸发罐实际使用情况为切入点,从2507双相不锈钢设备的使用环境和制作工艺两方面分析了钾盐蒸发罐发生腐蚀开裂现象的原因,进而讨论了如何在设计、制造及使用过程中避免双相不锈钢设备发生腐蚀。结果表明:双相不锈钢蒸发罐的使用环境和制造工艺均对其耐蚀性有很大的影响,尤其是当有焊接瑕疵和组装残余应力造成的应力集中,或在强酸、高温、高Cl~-含量介质溶液的环境中运行时,设备极易发生应力腐蚀裂纹。
[Abstract]:Based on the actual use of evaporator in two projects designed by a certain hospital, the causes of corrosion cracking of potash evaporator are analyzed from two aspects of using environment and manufacturing process of 2507 duplex stainless steel equipment. Furthermore, how to avoid corrosion of duplex stainless steel equipment during design, manufacture and operation is discussed. The results show that the use environment and manufacturing process of duplex stainless steel evaporator have great influence on its corrosion resistance, especially when the stress concentration caused by welding defects and assembly residual stress, or in strong acid, high temperature, The equipment is prone to stress corrosion cracking when running in the medium solution with high Cl~- content.
【作者单位】： 化工部长沙设计研究院;
【分类号】：TQ050.9

【相似文献】

相关期刊论文 前10条

1 李强;李小朋;徐承俊;;超级双相不锈钢薄壁储罐制作[J];石油化工建设;2012年04期

2 王湘平;;氮在奥氏体和双相不锈钢中的作用[J];化肥设计;1989年02期

3 秦紫瑞，李隆盛，贾克力，刘美云，，郭珊;结晶盐浆泵新型双相不锈钢的研究[J];化工机械;1994年03期

4 秦紫瑞,李隆盛,贾克力,刘美云,郭珊;耐硫酸及其盐腐蚀的新型双相不锈钢的研究[J];硫酸工业;1996年04期

5 刘福伦;双相不锈钢管在大型石化装置中的应用[J];石油化工设计;2003年01期

6 方伟秉;铁素体—奥氏体型双相不锈钢的焊接性[J];化工装备技术;1997年03期

7 刘晓娟;SAF2507双相不锈钢设备的设计、制造[J];化工设备设计;1999年03期

8 汪先锋;;母液蒸馏塔中双相不锈钢腐蚀浅析[J];纯碱工业;2006年06期

9 孙文山,丁桂荣,冯建中,高亮,侯孝礼,董进华,孙吉根,张享云;新型稀土双相不锈钢SG52在化学工业中的应用[J];硫酸工业;1998年02期

10 常春梅;张延丰;郭志军;姚田绪;;2205型双相不锈钢在板式热交换器中的应用[J];石油化工设备;2009年03期

相关重要报纸文章 前1条

1 刘翠珍;双相不锈钢在中国的应用及生产[N];世界金属导报;2002年

相关硕士学位论文 前2条

1 关祥丰;磷酸料浆泵叶轮用耐磨蚀双相不锈钢的研究[D];山东大学;2015年

2 孙玉芬;双相不锈钢光气反应器失效分析及其抗腐蚀性能研究[D];华东理工大学;2012年

本文编号：2205499