钡渣入场填埋前的预处理工艺条件研究

发布时间：2018-06-18 13:38

  本文选题：钡渣 + 预处理　； 参考：《武汉理工大学学报》2016年09期

【摘要】：通过钡渣预处理正交试验,分析浸取时间、液固比、搅拌速度及Na_2SO_4投加倍数对钡渣浸取液中Ba~(2+)浓度的影响,并对钡渣入场填埋前的预处理工艺条件进行初步探讨。结果表明,在浸取时间8h、液固比8∶1、搅拌速度5r/h、Na_2SO_4投加倍数为×2.2条件下,钡渣预处理脱Ba2+率高达90.65%,预处理后钡渣浸取液中Ba~(2+)浓度为102.8mg/L,满足钡渣入场填埋要求,减轻了后期淋溶液处理难度。
[Abstract]:The effects of leaching time, liquid-solid ratio, stirring speed and addition ratio of Na _ 2SO _ 4 on the concentration of Bazao _ 2) in barium slag leaching solution were analyzed by orthogonal experiment of barium slag pretreatment, and the pretreatment process conditions before barium slag entering landfill were preliminarily discussed. The results showed that when the leaching time was 8 h, the ratio of liquid to solid was 8: 1, and the mixing speed was 5 r / h, the multiple of adding Na2SO4 was 脳 2.2, the removal rate of Ba2 was as high as 90.65 and the concentration of Baan2 in the leachate was 102.8 mg / L, which met the requirement of barium slag entering the landfill. The difficulty of late leaching solution treatment was alleviated.
【作者单位】： 武汉理工大学土木工程与建筑学院;武汉理工大设计研究院有限公司;
【分类号】：X758

【相似文献】

相关期刊论文 前7条

1 王菊香;浅谈含砷金矿提金前的预处理工艺及合理选择[J];冶金矿山设计与建设;1997年06期

2 寇建军,朱昌洛;镇源金矿中性—氧化二步焙烧预处理工艺研究[J];矿产综合利用;2000年04期

3 余贵林;阳极泥预处理工艺探讨[J];江西铜业工程;1995年04期

4 李卫锋,赵占朝,蒋丽华;铅阳极泥浸出前预处理工艺评价[J];湿法冶金;1997年02期

5 李素梅，，廖昌盛;铁帽金矿浸前预处理工艺生产应用[J];黄金;1995年04期

6 王日;铜阳极泥预处理工艺优化[J];矿冶;2004年04期

7 ;[J];;年期

相关重要报纸文章 前4条

1 记者胡忠坤 通讯员李皓;云南冶金集团一研究成果通过专家鉴定[N];中国有色金属报;2008年

2 记者胡忠坤 通讯员李皓;云冶集团一项目通过专家鉴定[N];中国冶金报;2009年

3 闻哲;鞍钢首次实现船板预处理出口[N];中国船舶报;2011年

4 赵景山　于艳 首席记者 程云鹤;鞍钢船板首次实现预处理出口[N];鞍山日报　;2011年

本文编号：2035665