CTS-La复合物在废水处理及织物整理中的应用

发布时间：2018-08-21 08:32

【摘要】：以壳聚糖稀土复合物为原料,探讨了投加量、p H值等对印染废水处理效果的影响。结果表明,在室温条件下,壳聚糖和稀土氯化镧的质量比为2∶1,投加量为1.0 g/L,调节印染废水p H值至4.5左右,搅拌时间60 min时的处理效果最佳,印染废水的脱色率和COD去除率分别可达92.5%和83.6%。同时将CTS-La(Ш)复合物用于织物整理中,经9次洗涤后,对大肠埃希菌和金黄葡萄球菌的抑菌率仍可达99.09%和99.06%。
[Abstract]:Using chitosan rare earth complex as raw material, the effect of dosage of pH on the treatment of printing and dyeing wastewater was discussed. The results show that at room temperature, the mass ratio of chitosan to lanthanum chloride is 2: 1, the dosage is 1.0 g / L, the pH value of printing and dyeing wastewater is about 4.5, and the stirring time is 60 min. The decolorization rate and COD removal rate of printing and dyeing wastewater can reach 92.5% and 83.6% respectively. At the same time, the CTS-La compound was used in fabric finishing. After 9 times of washing, the bacteriostatic rates of Escherichia coli and Staphylococcus aureus were 99.09% and 99.06% respectively.
【作者单位】： 浙江万里学院生物与环境学院;
【基金】：宁波市自然科学基金(2015A610289) 国家级大学生创新创业训练计划项目(201510876003) 浙江省“生物工程”重中之重学科学生创新计划项目(CX2015020)
【分类号】：X791;TS195.2

【相似文献】

相关期刊论文 前10条

1 刘圣厚;张笑吟;刘楠;;印染废水排放及处理现状综述[J];科技视界;2014年08期

2 龚蕾蕾;;印染废水处理技术[J];广东化工;2014年09期

3 朱宏飞;李定龙;朱传为;;印染废水的危害及源头治理举措[J];环境科学与管理;2007年11期

4 徐志法;金城安;汪贤竹;付晓伟;金阳;;用K_2FeO_4去除印染废水COD的研究[J];广东化工;2013年19期

5 叶金兴;;酶在纺织工业中应用的最新研究进展[J];现代纺织技术;2007年04期

6 陈日旺;BOT模式在工业印染废水集中处理中的应用[J];国外建材科技;2005年04期

7 冯美丽;;A/O-MBR工艺处理印染废水的研究[J];河南科技;2014年07期

8 张艳,赵宜江,嵇鸣,仲慧;印染废水物理化学脱色方法的研究进展[J];水处理技术;2001年06期

9 林若舟;;真菌降解印染废水COD效应研究[J];北京农业;2011年06期

10 陆海燕;粉煤灰对工业废水净化作用的研究[J];天津轻工业学院学报;1999年01期

相关会议论文 前1条

1 张国徽;;印染废水的来源和特征分析[A];中国环境科学学会2006年学术年会优秀论文集（中卷）[C];2006年

相关硕士学位论文 前1条

1 张岩;改性麦麸对阴离子偶氮染料的吸附研究[D];华北电力大学(北京);2016年

，

本文编号：2195145