退火过程中聚乳酸中间相的形成和结构演化

发布时间：2018-06-05 11:45

  本文选题：聚乳酸 + 退火　； 参考：《高等学校化学学报》2016年03期

【摘要】：采用淬火法制备聚乳酸(PLA)非晶薄膜,并利用原位显微红外光谱在线研究PLA非晶薄膜在不同退火温度下的结构演化.结果表明,PLA非晶薄膜存在一个临界结晶温度,当退火温度高于临界结晶温度时,PLA非晶薄膜可以通过分子链的局部调整实现冷结晶,反之,不能发生冷结晶;在冷结晶过程中先出现中间相,随后发生中间相-晶体相的转变;中间相是通过分子链的构象调整和分子链间的堆砌调整产生的,退火温度越高,中间相出现得越早,最终得到的晶体结构越规整.
[Abstract]:Polylactic acid (PLA) amorphous films were prepared by quenching method. The structure evolution of PLA amorphous films at different annealing temperatures was studied by in situ microinfrared spectroscopy. The results show that there is a critical crystallization temperature in the PLA amorphous film. When the annealing temperature is higher than the critical crystallization temperature, the cold crystallization of the PLA amorphous film can be achieved by local adjustment of molecular chain, whereas cold crystallization cannot occur. In the cold crystallization process, the mesophase appears first, then the mesophase-crystal phase changes. The mesophase is produced by the conformation adjustment of molecular chain and the stacking adjustment between molecular chains. The higher the annealing temperature, the earlier the mesophase appears. The resulting crystal structure is more regular.
【作者单位】： 郑州大学力学与工程科学学院;郑州大学物理工程学院;郑州大学国家橡塑模具工程研究中心;
【基金】：国家自然科学基金(批准号:51573171)和国家自然科学基金重点项目(批准号:11432003)资助~~
【分类号】：O633.14

【相似文献】

相关期刊论文 前6条

1 熊新向,李轩科,杨栋梁,李清田;水性中间相制备的初步研究[J];炭素技术;1998年02期

2 李同起,王成扬;碳质中间相形成机理研究[J];新型炭材料;2005年03期

3 王茂章;;有机化合物的液相炭化化学[J];化学通报;1990年12期

4 钱树安;略论炭素科学的形成和进展──Ⅴ.液相炭化机理研究的历史和现状[J];炭素;1996年02期

5 常云峰,李柏龄,钱树安;中间相的分子结构[J];碳素;1986年03期

6 ;[J];;年期

相关博士学位论文 前1条

1 李同起;碳质中间相结构的形成及其相关材料的应用研究[D];天津大学;2005年

，

本文编号：1981880