空心玻璃微珠对陶瓷结合剂金刚石砂轮微观结构和力学性能的影响

发布时间：2018-02-02 08:32

  本文关键词： 空心玻璃微珠 陶瓷结合剂 金刚石砂轮 总气孔率 抗弯强度 硬度　出处：《工具技术》2017年10期 　论文类型：期刊论文

【摘要】：通过使用空心玻璃微珠作为造孔剂制备陶瓷结合剂金刚石砂轮,研究了不同含量和粒径的空心玻璃微珠对砂轮的总气孔率、抗弯强度、硬度以及微观结构的影响规律。试验结果表明:随着空心玻璃微珠含量的增加,砂轮总气孔率明显增加,抗弯强度和硬度显著下降;粗粒径(80μm)空心玻璃微珠陶瓷结合剂砂轮的抗弯强度和洛氏硬度略高于细粒径(40μm)砂轮的抗弯强度和洛氏硬度,但其总气孔率较细粒径砂轮更低。
[Abstract]:The total porosity and flexural strength of hollow glass beads on grinding wheels were studied by using hollow glass beads as pore-forming agent to prepare ceramic bond diamond grinding wheels. The experimental results show that with the increase of the content of hollow glass beads, the total porosity of grinding wheel increases obviously, and the bending strength and hardness decrease significantly. The bending strength and Rockwell hardness of the hollow glass bead ceramic bonded wheel are slightly higher than those of the fine grain diameter 40 渭 m) wheel. But its total porosity is lower than that of fine diameter grinding wheel.
【作者单位】： 广东工业大学;
【分类号】：TG743;TQ163
【正文快照】： 1引言随着科学技术的不断进步,各种新型陶瓷、复合材料、晶体材料、磁性材料在工业领域的应用越来越广泛,但其难加工的特性制约着这些材料的推。这些难加工材料的精密加工离不开金刚石砂轮。与树脂结合剂和金属结合剂金刚石砂轮相比,陶瓷结合剂金刚石砂轮具有自锐性强、易于修

【相似文献】

相关期刊论文 前10条

1 李立全;空心玻璃微珠[J];河南建材;2001年03期

2 徐美君;;秦皇岛建成空心玻璃微珠厂[J];建材工业信息;1990年15期

3 邓崇浩;许鑫华;;化学法在空心玻璃微珠制备中的应用[J];广州化工;2010年03期

4 彭寿;王芸;彭程;彭小波;;空心玻璃微珠制备方法及应用研究进展[J];硅酸盐通报;2012年06期

5 王元超;;空心玻璃微珠的开发与应用[J];船工科技;1984年02期

6 ;四种空心玻璃微珠复合新材料研制成功[J];船工科技;1985年02期

7 李秀云;;秦皇岛市玻璃厂已生产出空心玻璃微珠[J];建材工业信息;1991年10期

8 于o';空心玻璃微珠[J];建材工业信息;1996年10期

9 ;空心玻璃微珠将成为填充料新宠[J];技术与市场;2002年08期

10 刘亚辉;冯建林;许传华;;高性能空心玻璃微珠的应用研究[J];化学工程与装备;2011年05期

相关会议论文 前2条

1 王芸;彭程;彭小波;倪嘉;王华文;;空心玻璃微珠的应用研究现状[A];中国硅酸盐学会玻璃分会2009年全国玻璃科学技术年会论文集[C];2009年

2 彭小波;王芸;彭程;;空心玻璃微珠抗压强度检测方法及原理[A];2013全国玻璃科学技术年会论文集[C];2013年

相关硕士学位论文 前3条

1 赵可一;镀铜空心玻璃微珠的制备及其光催化性能的研究[D];华南理工大学;2016年

2 申娜娜;空心玻璃微珠轻质高强材料的制备与性能研究[D];天津大学;2014年

3 朱国庆;基于空心玻璃微珠功能微球的研究[D];西安工程大学;2012年

，

本文编号：1484085