纳米级掺合料粗合成纤维湿喷混凝土施工及抗裂性能分析

发布时间：2018-03-10 23:50

  本文选题：湿喷混凝土　切入点：纳米级掺合料　出处：《水电能源科学》2017年02期 　论文类型：期刊论文

【摘要】：为考察纳米级掺合料粗合成纤维湿喷混凝土的施工及抗裂性能,开展了凝结时间、回弹率、抗压强度、干缩、平板开裂和温度应力试验,并将其与同配制强度的硅粉钢纤维湿喷混凝土进行比较。结果表明,与硅粉钢纤维湿喷混凝土相比,纳米级掺合料粗合成纤维湿喷混凝土的凝结时间变化不大;回弹率下降了27%;1d抗压强度提高了45%;干缩测值接近,平板总开裂面积降低,温度应力开裂时间延长,开裂敏感性降低。
[Abstract]:In order to investigate the construction and crack resistance of nano-sized coarse synthetic fiber wet shotcreting concrete, tests of setting time, resilience, compressive strength, dry shrinkage, plate cracking and temperature stress were carried out. The results show that the setting time of nano-grade coarse synthetic fiber wet spray concrete is not changed compared with that of silica fume steel fiber wet spray concrete. The springback rate decreased by 27 / 1 and the compressive strength increased by 45.5%, the dry shrinkage value was close, the total cracking area of the plate was decreased, the time of thermal stress cracking was prolonged, and the cracking sensitivity was decreased.
【作者单位】： 南京水利科学研究院水文水资源与水利工程科学国家重点实验室;中国水利水电第七工程局有限公司;
【基金】：国家重点研发计划课题(2016YFC0401610) 江苏省自然科学基金项目(BK20151072) 中央级公益性科研院所基本科研业务费专项资金项目(Y416003) 中国水利水电第七工程局有限公司项目(2015-458-20)
【分类号】：TU528;TU755

【参考文献】

相关期刊论文 前10条

1 宁逢伟;陈波;简耀;;基于等强度设计的高性能混凝土抗裂性研究[J];人民长江;2015年24期

2 韩旭东;葛军;;纳米·增韧型粗纤维湿喷混凝土在锦屏二级水电站引水隧洞中的试验与应用[J];四川水力发电;2014年06期

3 黄秋丽;武选正;;XPM纳米材料在锦屏水电站辅助洞工程喷混凝土中的应用[J];四川水力发电;2013年S1期

4 赵路;;三板溪水电站泄洪洞衬砌混凝土温度应力影响因素分析[J];水力发电;2013年11期

5 陈波;孙伟;丁建彤;;温度-应力试验方法的建立[J];混凝土;2013年10期

6 张俊儒;;喷射混凝土单层衬砌抗渗机理及防水技术研究设想[J];重庆建筑;2013年09期

7 陈波;孙伟;丁建彤;;基于温度 应力试验的混凝土抗裂性研究进展[J];硅酸盐学报;2013年08期

8 欧阳幼玲;陈迅捷;陆采荣;方t，

本文编号：1595620