  本文选题：结合规律　切入点：自由氯离子　出处：《混凝土》2016年04期 　论文类型：期刊论文

【摘要】：为了研究水泥基复合材料中氯离子的结合规律,通过试验研究和理论分析得到PVA纤维水泥基中自由氯离子和结合氯离子关系,对于不同材料的水泥基,氯离子的结合规律也不相同。氯离子的结合关系会受到不同情况的影响,其中包括所处环境的温度和pH值,还有氯离子的浓度以及水泥基内部组成结构。结果表明:水泥基中自由氯离子和结合氯离子之间的关系随着浸泡时间的增加总体呈现线性增长趋势,纤维掺量的不同对于自由氯离子和结合氯离子的关系没有太大影响。
[Abstract]:In order to combine the study of chloride ion in cement-based composite materials, through the experimental study and theoretical analysis of free chloride ion of PVA fiber cement and chloride binding relationship for cement of different materials, combined with the law of chloride ion is not the same. Combined with the relationship of chloride ion will be affected by different conditions, including the environmental temperature and pH value, and the concentration of chlorine ion and cement internal structure. The results show that the cement based free chloride ion and chloride ion binding relationship between with increasing immersion time showed linear growth trend, the fiber content for free chloride ion and chloride ion binding of no too much impact.

【作者单位】： 内蒙古工业大学土木工程学院;内蒙古工业大学矿业学院;
【基金】：国家自然科学基金(51168033,51368041) 内蒙古自然科学基金(2012MS0706,2013MS0709) 内蒙古自治区高等学校科学研究项目(NJZY13104)
【分类号】：TU528

【参考文献】

相关期刊论文 前3条

1 吴相豪;周金岩;李怀垣;;环境因素影响粉煤灰混凝土固化氯离子能力的试验研究[J];粉煤灰;2011年05期

2 陈肇元;;钢筋的混凝土保护层设计要求急待改善——混凝土结构设计规范的问题讨论之一[J];建筑结构;2007年06期

3 宋玉普,宋立元,赵敏;混凝土海洋平台抗氯离子侵蚀耐久寿命预测试验研究[J];大连理工大学学报;2005年05期

相关博士学位论文 前1条

1 金祖权;西部地区严酷环境下混凝土的耐久性与寿命预测[D];东南大学;2006年

相关硕士学位论文 前1条

1 叶海隆;混凝土裂缝对氯离子传输及水分影响深度的研究[D];浙江大学;2013年

【共引文献】

相关期刊论文 前10条

1 刘曙光;李海林;张菊;闫长旺;鲁小宇;;PVA纤维水泥基复合材料中氯离子结合能力[J];混凝土;2016年04期

2 闫长旺;李杰;张菊;刘曙光;;西部氯盐渍土介质中混凝土的氯离子扩散性[J];功能材料;2016年02期

3 王立成;鲍玖文;李淑红;;损伤混凝土毛细吸水性能试验研究和水分分布预测分析[J];大连理工大学学报;2015年06期

4 冉坤;;无机矿物聚合物混凝土氯离子渗透性的研究[J];山西建筑;2015年23期

5 黄凤凤;苏楠楠;张强;刘海鹏;石志慧;董晓强;;氯化钠溶液对水泥砂浆的腐蚀行为[J];科学技术与工程;2015年20期

6 范宏;阚积鹏;张鑫;;钢筋混凝土构件中垫块和马凳设置标准化研究[J];建筑技术;2015年06期

7 张广泰;董海蛟;温勇;;冻融循环下锂渣粉对混凝土渗透性的影响[J];混凝土与水泥制品;2015年03期

8 温勇;李文婷;邓U，

本文编号：1643639