秸秆造孔剂对页岩烧结微孔砖工艺性能的影响研究

发布时间：2018-04-01 16:34

  本文选题：页岩烧结微孔砖　切入点：秸秆造孔剂　出处：《施工技术》2017年16期

【摘要】：以页岩和秸秆造孔剂作为原材料,探究不同掺量、不同粒径范围的秸秆造孔剂对页岩烧结微孔砖在抗压强度、体积密度、吸水率、显气孔率等方面的影响规律。试验结果表明:随着秸秆粉末掺量的增多和粒径的增大,试件标准稠度用水量增多,抗压强度降低和体积密度降低,显气孔率升高。通过控制秸秆粉末的掺量和粒径,能有效地改善页岩烧结砖的各项性能。
[Abstract]:Using shale and straw pore-making agent as raw materials, the compressive strength, volume density and water absorption of shale sintered microporous brick with different content and different particle size range of straw pore-making agent were investigated. The experimental results show that with the increase of the amount of straw powder and the increase of particle size, the standard consistency water consumption increases, the compressive strength decreases and the volume density decreases. By controlling the content and particle size of straw powder, the properties of shale sintered brick can be improved effectively.
【作者单位】： 西南科技大学土木工程与建筑学院;
【基金】：国家自然科学基金“青年基金”项目(11502219) 西南科技大学创新基金项目(17ycx099)
【分类号】：TU522.1

【相似文献】

相关期刊论文 前5条

1 康庆庆;王庆伟;王勇峰;祝聿霏;;不同造孔剂对煤矸石合成多孔莫来石性能影响的研究[J];中国陶瓷;2012年06期

2 梁小平,靳正国,朱春华,胡在华;造孔剂对多孔Al_2O_3陶瓷性能的影响[J];天津工业大学学报;2005年03期

3 伍协;陈振华;冯延林;刘小磐;李秀莉;;采用布纤维做造孔剂制备微蜂窝陶瓷(英文)[J];Transactions of Nonferrous Metals Society of China;2011年12期

4 李娜,王超,朱苏敏,王若钉;聚乙二醇作造孔剂制备大孔溶胶凝胶生物活性玻璃[J];无机化学学报;2005年01期

5 于波;张文强;梁明德;张平;徐景明;;PMMA造孔剂对固体氧化物电解池制氢性能的影响[J];无机材料学报;2011年08期

，

本文编号：1696348