大掺量陶瓷抛光废粉绿色混凝土的配制和性能

发布时间：2018-04-13 08:33

  本文选题：陶瓷抛光废粉 + 粗粉煤灰　； 参考：《混凝土》2017年11期

【摘要】：为提高工业固体废弃物的利用水平,优化配合比了复掺陶瓷砖抛光废粉及粗粉煤灰的绿色混凝土(GPFC),总掺量为0~60%。观测了GPFC混凝土的黏聚性、流动性、保水性等工作性能,获得了不同混凝土的3、7、28 d强度。研究表明,水胶比为0.24~0.57时,变化配合比参数,GPFC可保持基本一致的工作性。60%掺量时,类似工作性的GPFC混凝土较普通混凝土(NC)可降低水泥用量24%以上,早期强度提高11%以上。研究可为陶瓷抛光废粉以较大掺量用于混凝土提供试验参考。
[Abstract]:In order to improve the utilization level of industrial solid waste, the proportion of green concrete mixed with ceramic tile polishing waste powder and coarse fly ash was optimized.The cohesion, fluidity and water retention properties of GPFC concrete were observed, and the strength of different concrete was obtained.The results show that when the ratio of water to binder is 0.24 ~ 0.57, the ratio of GPFC concrete with similar workability can be reduced by more than 24% and the early strength of GPFC concrete can be increased by more than 11% when the ratio of water to binder is 0.24 ~ 0.57, and the workability of GPFC concrete with similar workability is almost the same as that of ordinary concrete.The study can provide experimental reference for ceramic polishing waste powder used in concrete.
【作者单位】： 山东理工大学建筑工程学院;山东天齐置业集团股份有限公司;
【基金】：山东省中青年科学家奖励基金项目(BS2009CL046) 深圳土木工程耐久性重点实验室开放课题项目(SZDCCE2010)
【分类号】：TU528

【相似文献】

相关期刊论文 前10条

1 周良;;关于绿色混凝土“绿色"内涵的思考[J];江苏建材;2005年04期

2 周良;;关于绿色混凝土“绿色”内涵的思考[J];中国建材科技;2006年01期

3 陈明宇;;绿色混凝土的发展与应用[J];山西建筑;2013年27期

4 艾红梅;白军营;;环境协调型绿色混凝土的发展[J];混凝土;2010年12期

5 夏远英;陈景;熊骁辉;郑广军;;绿色混凝土发展途径的探讨[J];混凝土;2011年04期

6 张遵海;孙文标;田坤云;;绿色混凝土的水化硬化特征研究[J];混凝土;2011年07期

7 谭洪光;;绿色混凝土的若干问题[J];建材发展导向;2011年06期

8 孙泽田;杨树桐;;实现绿色混凝土的新途径[J];混凝土;2013年12期

9 ;坚而不摧:古罗马防波堤为绿色混凝土提供新思路[J];商品混凝土;2013年11期

10 张斌;;绿色混凝土在建筑工程中的应用[J];建设科技;2014年10期

相关会议论文 前1条

1 周述光;;CMA生物灰代替水泥制作绿色混凝土的技术可行性研究[A];2011年混凝土与水泥制品学术讨论会论文集[C];2011年

相关硕士学位论文 前3条

1 李龙浩;新型绿色混凝土速凝剂的设计与制备[D];湖南师范大学;2015年

2 张磊;基于灰色系统理论的绿色混凝土综合评价[D];兰州交通大学;2015年

3 和园园;绿色混凝土复合自保温砌块研制[D];山东建筑大学;2016年

，

本文编号：1743721