硫酸浸取法提取一水硬铝石中氧化铝工艺研究

发布时间：2018-04-13 16:40

  本文选题：铝土矿 + 一水硬铝石　； 参考：《矿冶工程》2017年02期

【摘要】：以低品位的一水硬铝石型铝土矿为原料,对硫酸浸取法提取铝土矿中氧化铝的工艺进行了研究。通过单因素实验和正交实验研究了硫酸浸取法提取铝土矿中氧化铝过程中硫酸浓度、反应时间、反应温度和液固比对氧化铝溶出率的影响。结果表明,在硫酸浓度90%、反应温度180℃、液固比8∶1、加热时间120 min的条件下,氧化铝相对溶出率达到90.23%以上。该工艺在常压下进行,对铝土矿的开发利用具有重要意义。
[Abstract]:With diaspore type bauxite low grade as raw material, process of sulfuric acid leaching of alumina from bauxite extraction were studied. The concentration of sulfuric acid, leaching alumina from bauxite in the extraction process of sulfuric acid were studied by single factor and orthogonal experiments of reaction time, reaction temperature and liquid-solid ratio on the leaching rate of alumina the effects of sulfuric acid concentration. The results showed that in 90%, the reaction temperature is 180 DEG C, liquid-solid ratio of 8: 1, 120 min under the condition of heating time, relative alumina dissolution rate reached above 90.23%. The process was carried out under atmospheric pressure, is of great significance to the development and utilization of bauxite.

【作者单位】： 贵州师范大学材料与建筑工程学院;桂林电子科技大学广西信息材料重点实验室;
【基金】：贵阳市白云区科技计划项目(白科合同[2013]号) 广西信息材料重点实验室开放研究基金(161005-K) 贵州师范大学博士启动金项目
【分类号】：TQ133.1

【相似文献】

相关期刊论文 前7条

1 李浩群,邵天敏,陈大融;一水硬铝石热分解动力学研究[J];硅酸盐学报;2002年03期

2 杨华明,胡岳华,杨武国,杜春芳,邱冠周;一水硬铝石的机械化学处理(英文)[J];硅酸盐学报;2005年06期

3 季先德;论我国一水硬铝石矿的拜耳法强化溶出工艺[J];有色金属(冶炼部分);1998年06期

4 杨静;周海波;李玉茹;王悦;黄宝贵;;某低品位复杂铝土矿中高岭石与一水硬铝石的分离方法问题研究[J];中国无机分析化学;2014年01期

5 陈松涛,马步伟,赵振新,郑海金;利用一水硬铝石制备精制硫酸铝工艺研究[J];河南城建高等专科学校学报;1999年01期

6 马朝建,赵岗;用我国中低品位一水硬铝石矿生产氧化铝的新方法[J];轻金属;1998年12期

7 ;[J];;年期

，

本文编号：1745332