第一步离子交换时间对化学钢化玻璃的性能影响

发布时间：2018-04-19 06:12

本文选题：化学钢化 + 离子交换时间　；参考：《硅酸盐通报》2016年06期

【摘要】：本文主要研究化学钢化玻璃中第一步离子交换的时间对化学钢化玻璃的性能影响。制备出不同的离子交换时间的化学钢化玻璃。分析第一步交换时间对钢化玻璃的弯曲强度、Weibull模数、表面应力大小、深度以及K+离子扩散所产生的影响。结果表明:随着第一步离子交换时间的延长,弯曲强度逐渐降低,Weibull先升高后降低,在40h时达到最高值;表面应力大小会随着时间的延长而降低,应力深度会增加;K+离子扩散曲线符合菲克第二定律的拟合曲线。扩散深度随着时间增加而增加,并且会在玻璃内部产生富集峰。
[Abstract]:The effect of the first step ion exchange time on the properties of chemically toughened glass was studied in this paper.Chemical toughened glass with different ion exchange time was prepared.The effects of the first step exchange time on the bending strength Weibull modulus, surface stress, depth and K ion diffusion of toughened glass are analyzed.The results show that with the prolongation of the first step ion exchange time, the bending strength of Weibull increases first and then decreases, and reaches the maximum value at 40 h, and the surface stress decreases with the time.The stress depth increases the fitting curve of K ion diffusion curve in accordance with Fick's second law.The diffusion depth increases with time, and the enrichment peak occurs in the glass.
【作者单位】：武汉理工大学材料科学与工程学院;武汉理工大学硅酸盐建筑材料国家重点实验室;
【基金】：“十二五”国家科技支撑计划(2012BAA08B04)资助
【分类号】：TQ171.732

【相似文献】