高纯二硫化钼深度除铁新工艺研究

发布时间：2018-04-20 23:00

  本文选题：钼精矿 + 高纯二硫化钼　； 参考：《无机盐工业》2017年11期

【摘要】：以钼精矿为原料,改变传统多段酸浸多次水洗除铁工艺,通过加入自制的复合助溶剂,采用低温常压一段酸浸一次水洗方法,将二硫化钼中铁的质量分数由1.0%左右降至0.10%以下。最佳的反应温度为75℃,反应时间为2.5 h,助溶剂用量为9%(以钼精矿质量计)。产品按GB/T 23271—2009《二硫化钼》方法检测,产品中Mo、Fe、MoO_3的质量分数分别为57.8%、0.04%、0.05%,酸值为(酸值为中和脂肪、脂肪油或其他类似物质1 g中含有的游离脂肪酸所需氢氧化钾的质量,mg)0.03 mg/g,总收率为96.5%。
[Abstract]:Using the molybdenum concentrate as the raw material, the traditional multi acid leaching process of water washing and removing iron is changed. The mass fraction of iron in molybdenum disulfide is reduced from about 1% to less than 0.10% by adding the self-made compound cosolvent, the mass fraction of iron in molybdenum disulfide is reduced from about 1% to 0.10%. The optimum reaction temperature is 75, the reaction time is 2.5, and the dosage of the cosolvent is 9%. The product is measured by GB/T 23271 - 2009< molybdenum disulfide method. The mass fraction of Mo, Fe, and MoO_3 in the product is 57.8%, 0.04%, 0.05% respectively. The acid value is the mass of the potassium hydroxide for the free fatty acid contained in the 1 g of the fatty oil or other similar substances, Mg) 0.03 mg/g, with the total yield of 96.5%.

【作者单位】： 河南省化工研究所有限责任公司;河南省精细化工中间体工程技术研究中心;洛阳申雨钼业有限责任公司;
【分类号】：TQ136.12

【相似文献】

相关期刊论文 前10条

1 李景恒;姚会民;董永芳;;改进过筛除铁工艺 提高产品质量[J];电瓷避雷器;1989年02期

2 邵行易;;谈谈电瓷生产中的泥浆过筛除铁[J];电瓷避雷器;1992年03期

3 黄耀林;叶富华;杜昆;朱曼密;;工业硫酸铜深度除铁工艺的研究[J];材料研究与应用;2012年04期

4 吕德全,左玖玲,曲江;除铁方法在生产工艺中的应用探讨[J];化学工程师;2005年08期

5 余健;禹丽娥;任文辉;;地下水生物除铁的效果及机理验证[J];工业用水与废水;2006年02期

6 刘俊峰,易平贵,陈安国;硫酸锌生产除铁工艺及其比较[J];无机盐工业;2001年01期

7 魏盼中;周涛;许海曼;杨静思;;高岭土除铁增白的实验研究[J];中国粉体技术;2010年03期

8 聂莎;潘祺;邵后东;沈毅;;江西临川高岭土除铁增白研究[J];陶瓷学报;2014年03期

9 赵昱;;直接钼蓝光度法测定高纯二硫化钼中微量硅[J];中国钼业;2006年04期

10 郭英姿;王鹏;;氨法焙烧粉煤灰浸出液联合法除铁工艺研究[J];轻金属;2014年04期

相关会议论文 前1条

1 李泽;;日用瓷、卫生洁具、建筑陶瓷产品生产中的除铁[A];中国硅酸盐学会陶瓷分会机械装备专业委员会2006学术年会论文集[C];2006年

相关重要报纸文章 前1条

1 陶吉;BK系列陶瓷原料除铁设备[N];广东建设报;2004年

，

本文编号：1779803