基于低含量合成骨粉的日用陶瓷制备与性能研究

发布时间：2018-04-22 20:32

  本文选题：合成骨粉 + 抗弯强度　； 参考：《中国陶瓷》2017年09期

【摘要】：基于环保、资源和成本方面的考虑,以降低现有骨质瓷配方中骨粉含量为目的,通过配方优化和原料精选,研究了低含量合成骨粉的日用陶瓷制备与性能。设计了合成骨粉用量在0~10 wt%范围的陶瓷坯体组成及其制备工艺,并对烧成的瓷坯进行了抗折强度、透过率、密度、吸水率和物相等测试和分析。结果表明,合成骨粉含量6 wt%的坯体抗折强度高达175 MPa、光透过率达到9.5%/2 mm,该瓷器具备良好的市场前景和社会价值。
[Abstract]:Based on the consideration of environmental protection, resources and cost, the preparation and properties of domestic ceramics with low content of synthetic bone powder were studied by optimizing the formula and selecting the raw materials for the purpose of reducing the content of bone powder in the existing bone ceramic formulations. The composition and preparation process of ceramic billet with the amount of synthetic bone powder in the range of 0 ~ 10 wt% were designed. The bending strength, transmittance, density, water absorption and material equality of the sintered ceramic blank were tested and analyzed. The results show that the bending strength of the body with 6 wt% bone powder is 175 MPA and the light transmittance reaches 9.5 / 2 mm. The porcelain has a good market prospect and social value.
【作者单位】： 南京工业大学材料科学与工程学院;
【分类号】：TQ174.73

【相似文献】

相关期刊论文 前9条

1 顾秀超;;膜透过率测定法[J];陕西化工;1986年01期

2 陈向飞;李卫红;;影响光伏压延玻璃透过率的原因分析与对策[J];玻璃;2013年12期

3 江华,徐勇,勇强,余世袁;木聚糖溶液超滤透过率的研究[J];林产化学与工业;2000年04期

4 陈新政;王海风;;透远紫外玻璃中痕量铁对紫外透过率的影响[J];玻璃与搪瓷;2011年04期

5 杨富国,方正,徐勇,毛连山,余世袁,朱琼霞;木聚糖碱抽提液超滤过程中的溶剂透过率[J];中南工业大学学报(自然科学版);2003年01期

6 朱斐章,何美玉,贺仪雍;矫正感光元件滤光玻璃的研制[J];玻璃与搪瓷;1989年01期

7 罗春炼;韩文爵;王海风;胡沛然;;提高防眩玻璃透过率的主要影响因素[J];化工新型材料;2008年12期

8 ;高透过率玻璃[J];机电新产品导报;1994年05期

9 王承遇,陶瑛;玻璃成分的设计与调整(二十三)[J];玻璃与搪瓷;2005年05期

相关博士学位论文 前1条

1 柯瑞;辐照/压痕载荷/表面图形化条件下蓝宝石单晶性能研究[D];哈尔滨工业大学;2014年

相关硕士学位论文 前1条

1 刘晏;提高激光陶瓷透明度的机理和技术研究[D];西安电子科技大学;2014年

，

本文编号：1788813