脱硫石膏灌芯墙干燥时间影响因素分析

发布时间：2018-08-20 13:31

【摘要】：通过采用不同厚度的脱硫石膏浆样品,改变珍珠岩掺量和环境相对湿度,覆盖纸面石膏板对石膏浆体干燥蒸发过程进行实验比较分析。结果表明,脱硫石膏浆体的干燥时间与其厚度呈现非线性增长关系;珍珠岩掺量却对脱硫石膏浆体干燥行为影响较小;环境相对湿度的增加显著延长了石膏浆体的干燥时间,环境相对湿度从55%增加到75%时,脱硫石膏浆体完全干燥时间延长了近1倍;纸面石膏板的覆盖在高环境相对湿度(75%)下对脱硫石膏的干燥时间影响较小,但在低环境相对湿度(55%)下干燥时间急剧延长,可达2倍。
[Abstract]:The drying evaporation process of gypsum slurry was studied by using different thickness samples of desulphurized gypsum slurry by changing perlite content and relative humidity of environment and covering paper gypsum board. The results show that the drying time of desulphurized gypsum slurry has a nonlinear relationship with its thickness, the perlite content has little effect on the drying behavior of desulphurized gypsum slurry, and the drying time of desulphurized gypsum slurry is significantly prolonged with the increase of relative humidity in the environment. When the relative humidity increased from 55% to 75%, the drying time of desulphurized gypsum slurry was nearly doubled, and the drying time of desulphurized gypsum was less affected by the covering of plasterboard with high relative humidity (75%). However, the drying time at low relative humidity (55%) was prolonged sharply, up to 2 times.
【作者单位】： 东华理工大学建筑工程学院;华东交通大学土木建筑学院;同济大学先进土木工程材料教育部重点实验室;
【基金】：江西省自然科学基金项目(20151BAB213023)
【分类号】：TQ177.377

【参考文献】

相关期刊论文 前7条

1 夏纯洁;周觅;沈琴芳;王小燕;王婷;;重量法测定石膏中三氧化硫的不确定度评定[J];化学通报;2015年02期

2 莫建松;杨有余;盛海强;刘兴利;翟春丰;程常杰;;脱硫石膏粒径分布与脱水性能实验研究[J];环境工程学报;2013年11期

3 王兰馨;赵忠兴;耿德军;;添加剂对石膏型强度的影响[J];沈阳理工大学学报;2009年06期

4 王兵;;功能性纸面石膏板的应用及发展潜力[J];新型建筑材料;2009年10期

5 康燕;靳玉春;;石膏型干燥工艺研究[J];铸造设备与工艺;2009年05期

6 赵忠兴;石颖科;叶锦华;;石膏型快速烘干工艺的研究[J];特种铸造及有色合金;2008年06期

7 关淑君;耐水建筑石膏的试验研究[J];新型建筑材料;2005年02期

相关硕士学位论文 前1条

1 康燕;石膏型混合料工艺性能研究[D];中北大学;2010年

【共引文献】

相关期刊论文 前10条

1 崔强;高超;陈富强;孔令才;杨大田;卿丽雅;;石灰岩机制砂砂浆的干缩与耐磨性能[J];山东交通学院学报;2017年02期

2 戴浩;刘艳;王中兰;李东旭;;面层自流平砂浆的耐磨性能研究[J];新型建筑材料;2017年06期

3 潘玲;杨成军;;预处理磷石膏在自流平材料中的应用[J];非金属矿;2017年03期

4 杭美艳;路兰;郝小龙;;复合外加剂对以钢板为粘结基层的干混砂浆性能影响研究[J];混凝土世界;2017年03期

5 韩芳芳;高奎e，

本文编号：2193791