反应物浓度对氢氧化镁沉降性能和粒度的影响

发布时间：2018-10-14 10:59

【摘要】：利用氯化镁和电石渣制备镁质胶凝材料所用氧化镁,生产原料廉价,产品用途广泛,具有很大的应用价值。研究了常温下反应物浓度对氢氧化镁沉降和粒度的影响,结果表明:氯化镁和电石渣摩尔比例为1.25∶1,氯化镁浓度为1.875 mol/L时,氢氧化镁料浆沉降速率和平均粒度相比与其他浓度最大,为工业生产提供研究基础。
[Abstract]:Magnesium oxide used in the preparation of magnesia cementitious materials from magnesium chloride and calcium carbide slag is of great application value because of its cheap raw materials and widely used products. The effect of reactant concentration on the deposition and particle size of magnesium hydroxide at room temperature was studied. The results showed that the molar ratio of magnesium chloride to calcium carbide slag was 1.25: 1, and the concentration of magnesium chloride was 1.875 mol/L. Compared with other concentration, magnesium hydroxide slurry sedimentation rate and average particle size are the largest, which provides a basis for industrial production.
【作者单位】： 中国科学院大学;中国科学院青海盐湖研究所;青海盐湖工业股份有限公司;
【基金】：青海省重大科技专项(2015-GX-A1A)
【分类号】：TQ132.2

【相似文献】

相关期刊论文 前10条

1 王从俊;梁柏青;;反应速度新议[J];化学教育;1992年05期

2 ;征答(25)[J];大学化学;1990年02期

3 姜义兴;王乃魁;丁进;;氢氮比自调系统[J];化工自动化及仪表;1982年03期

4 吴小庆;;对酸化过程表面反应理论的研究[J];石油学报;1990年02期

5 林凯;;反应物质的浓度、温度影响反应速度的实验——亚硫酸氢钠与碘酸钾相互作用的课堂演示[J];化学通报;1957年12期

6 严宣申;;关于氢氧化铜与氨水的反应[J];化学教育;1988年05期

7 王挺;蒋新;刘斐;;反应物的变化对吸附相反应技术制备NiO/SiO_2的影响[J];无机化学学报;2009年01期

8 谢毅;袁鸽成;郑勇;倪学明;冷文兵;;反应物浓度对液相合成Al_2O_3-SiO_2-CaF_2-P_2O_5系粉体特性的影响[J];广东工业大学学报;2008年02期

9 周宏明;曾麟;易丹青;郭雁军;贾晓慧;刘珊;何俊杰;;FHA粉末的制备及相结构和热稳定性[J];中南大学学报(自然科学版);2011年05期

10 郑锡荣;;利用正电子发射研究表面催化作用[J];化学通报;1993年12期

相关会议论文 前4条

1 陈U，

本文编号：2270250