锂渣混凝土孔分形维数与气体渗透性能关系研究

发布时间：2019-03-26 20:08

【摘要】：利用压汞法(MIP)测试了不同锂渣掺量的C30、C60混凝土的孔结构参数,计算了被测混凝土的孔体积分形维数、孔轴线分形维数,并研究了混凝土气体渗透系数、锂渣掺量与孔体积分形维数、孔轴线分形维数之间的关系。结果表明,混凝土的气体渗透系数与孔体积分形维数相关性高;C60混凝土在锂渣掺量为10%时,孔体积分形维数和孔轴线分形维数最大;随着锂渣掺量的提高,C30混凝土孔体积分形维数和孔轴线分形维数呈降低的趋势。
[Abstract]:The pore structure parameters of C30 and C60 concrete with different lithium slag content were measured by mercury pressure method (MIP). The pore volume fractal dimension and pore axis fractal dimension of the measured concrete were calculated, and the gas permeability coefficient of the concrete was studied. The relationship between lithium slag content and pore volume fractal dimension and pore axis fractal dimension. The results show that the gas permeability coefficient of concrete is highly correlated with the fractal dimension of pore volume, and the fractal dimension of pore volume and axis of C60 concrete is the largest when the content of lithium slag is 10%. With the increase of lithium slag content, the pore volume fractal dimension and pore axis fractal dimension of C30 concrete decrease.
【作者单位】： 新疆大学建筑工程学院;
【基金】：国家自然科学基金(51268055)
【分类号】：TU528

【相似文献】

相关期刊论文 前10条

1 韦江雄;余其俊;曾小星;白瑞英;;混凝土中孔结构的分形维数研究[J];华南理工大学学报(自然科学版);2007年02期

2 郑乃章;黄荣;熊春华;苗立峰;莫云杰;朱小平;;不同条件下硅酸锌结晶形貌的分形维数[J];中国陶瓷;2009年09期

3 李新梅,王勇,韩涛;瓷釉涂层/金属基体界面分形维数的研究[J];硅酸盐通报;2005年02期

4 秦朝燕;邱祖民;陈文有;;絮凝体的三维DLA模型分形模拟[J];南昌大学学报(工科版);2010年02期

5 王婷;周丹丹;董双石;郑文宇;杨毅;;锥形流化床混凝装置内混凝指标和絮凝体分形维数[J];化工学报;2010年05期

6 吴秋林;吴邦明;彭美生;赵瑞兰;;多孔膜成孔机理的分形研究[J];水处理技术;1993年04期

7 李永鑫,陈益民,贺行洋,韦江雄,张文生,张洪滔,郭随华;粉煤灰-水泥浆体的孔体积分形维数及其与孔结构和强度的关系[J];硅酸盐学报;2003年08期

8 缪明烽,沈湘林;钙基脱硫剂孔隙分形特性的实验研究[J];热能动力工程;2001年06期

9 朱明;胡曙光;贺振华;;硅酸盐水泥的理化性能与分形维数研究[J];武汉理工大学学报;2008年05期

10 缪明烽,沈湘林;钙基脱硫剂分形孔结构的实验研究[J];能源研究与利用;2001年01期

相关会议论文 前1条

1 汪洋;徐玲玲;吴国辉;刘明帝;魏艳玲;;水泥粒度分布的分形维数与其特征参数的关系[A];2011中国材料研讨会论文摘要集[C];2011年

相关硕士学位论文 前1条

1 刘建;水泥回转窑故障诊断系统研究[D];天津理工大学;2015年

，

本文编号：2447884