海水环境下2024铝合金腐蚀磨损性能研究

发布时间：2018-01-01 00:33

本文关键词：海水环境下2024铝合金腐蚀磨损性能研究　出处：《中国腐蚀与防护学报》2016年06期 　论文类型：期刊论文

【摘要】：采用往复式销盘摩擦试验机和电化学工作站研究了2024铝合金/Al_2O_3陶瓷在海水环境下的腐蚀磨损行为以及腐蚀磨损之间的交互作用。结果表明:在模拟海水实验条件下,2024铝合金在开路电位下的腐蚀磨损量明显大于其在阴极保护条件下的磨损量,说明腐蚀与磨损发生交互作用。纯磨损量约占总腐蚀磨损量的比例(W_0/T)为70.3%~98.2%,在腐蚀磨损过程中磨损作用明显大于腐蚀作用。腐蚀磨损交互作用量占总腐蚀磨损量的比例(S/T)为1.8%~29.7%,腐蚀磨损交互作用同样不可忽视。
[Abstract]:By using a reciprocating pin on disc friction tester and electrochemical workstation 2024 Aluminum Alloy /Al_2O_3 ceramics in the marine environment corrosion wear behavior and corrosion wear interaction. The results show that in simulated seawater under the experimental conditions, 2024 Aluminum Alloy corrosion at open circuit potential is obviously greater than that of the wear amount under the condition of cathodic protection wear that amount of corrosion and wear interaction. The pure wear volume accounted for the proportion of the total amount of corrosion and wear (W_0/T) for 70.3%~98.2% in corrosion wear was obviously better than corrosion. Corrosion wear interaction accounted for the total amount of corrosion and wear ratio (S/T) for 1.8%~29.7%, the same can not be ignored the corrosion wear interaction role.

【作者单位】：江西理工大学材料科学与工程学院;中国科学院宁波材料技术与工程研究所中国科学院海洋新材料与应用技术重点实验室浙江省海洋材料与防护技术重点实验室;
【基金】：宁波市自然科学基金项目(2016A610263) 国家重点基础研究发展计划项目(2014CB643302)资助
【分类号】：TG172.5
【正文快照】： 2.中国科学院宁波材料技术与工程研究所中国科学院海洋新材料与应用技术重点实验室浙江省海洋材料与防护技术重点实验室宁波3152011前言铝合金具有较低的密度、良好的力学性能、加工性能、导热性、导电性以及耐蚀性和低成本等一系列优点,在船用设备领域中的应用日趋广泛,对减