湿喷丸强化对TC4钛合金表面状态及疲劳性能的影响

发布时间：2018-01-02 11:29

本文关键词：湿喷丸强化对TC4钛合金表面状态及疲劳性能的影响　出处：《金属热处理》2016年03期 　论文类型：期刊论文

更多相关文章： TC合金 湿喷丸 表面状态 疲劳性能

【摘要】：采用陶瓷湿喷丸强化技术对TC4合金进行表面改性处理,研究湿喷丸强度对钛合金表面状态及拉拉疲劳寿命的影响规律。结果表明,湿喷丸强化在材料表面引入残余压应力场,随喷丸强度增加残余压应力层变深。喷丸强度为0.1~0.2 mm N时,材料表面机加工痕迹得到有效去除,且表面粗糙度降低。湿喷丸强化后,材料表层位错密度增加,晶粒细化。湿喷丸强化能够明显改善TC4合金疲劳性能,改善效果和喷丸强度间不是单调关系,即存在最优喷丸工艺参数。在喷丸强度0.3 mm N条件下,疲劳寿命是基材的1.93倍,改善效果最明显。
[Abstract]:The ceramic wet shot peening surface modification of TC4 alloy, the influence of shot peening intensity on the wet surface of the titanium alloy and the life state of tension fatigue. The results showed that the wet shot peening on the surface of the material into the residual stress field and residual compressive stress layer becomes deeper with increasing peening intensity. Shot peening intensity is 0.1~0.2 mm N, the material surface machining marks are effectively removed, and the surface roughness decreased. After the wet shot peening, dislocation density increases and the material grain refinement. Wet shot peening can improve the fatigue properties of TC4 alloy, and improve the effect of shot peening intensity is not monotonic, i.e. the existence of the optimal process parameters. In the shot peening the intensity of 0.3 mm under the condition of N, the fatigue life is 1.93 times of the substrate, the most obvious improvement effect.

【作者单位】：大连理工大学材料科学与工程学院;北京航空制造工程研究所;
【基金】：中国博士后科学基金(2014M551074)
【分类号】：TG668
【正文快照】： TC4钛合金由于其密度小、比强度高、中温稳定性以及优异的耐腐蚀等性能,在航空航天领域有着比较广泛的应用。但其硬度低、耐磨性差、疲劳强度低等缺点限制了其进一步发展应用[1]。仅仅依靠钛合金自身固有的疲劳抗力难以满足航空结构件长寿命、高可靠性及高安全性的设计要求,为

【参考文献】