不同焊接方法对09CuPCrNi薄板搭接接头组织和性能的影响

发布时间：2018-01-14 11:08

  本文关键词：不同焊接方法对09CuPCrNi薄板搭接接头组织和性能的影响　出处：《电焊机》2016年11期 　论文类型：期刊论文

  更多相关文章： CuPCrNi 薄板搭接接头 电阻点焊 胶接点焊 塞焊

【摘要】：采用电阻点焊、胶接点焊和塞焊三种焊接方法,对3mm+3mm 09CuPCrNi钢搭接接头的组织和力学性能进行对比研究。结果表明:三种焊接方法下焊接接头的剪切拉伸性能均满足标准,其中塞焊时接头剪切拉伸性能较好;电阻点焊和胶接点焊接头各区域硬度相近且高于塞焊下接头各区域硬度;塞焊接头的组织与电阻点焊和胶接点焊接头组织有所不同;点焊及胶接点焊焊接接头的熔透率均满足相关标准。
[Abstract]:The resistance spot welding, weld bonding and plug welding three welding methods, comparative study on Microstructure and mechanical properties of 3mm+3mm steel 09CuPCrNi joint. The results showed that three kinds of welding methods under tensile and shear properties of welded joints can meet the standard, the plug welding joint tensile shear performance; resistance spot welding and weld bonding the hardness of the area near and above the joint plug welding joints under the hardness; plug welding joint microstructure and resistance spot welding and bonding spot welded joint microstructure different; spot welding and weld bonding welding penetration rate all meet the relevant standards.

【作者单位】： 中车唐山轨道客车有限责任公司;
【分类号】：TG407
【正文快照】： 0前言近年来随着我国铁路事业蓬勃发展,不仅对机车内部制造有着严格的要求,对外观质量的要求也逐渐提高。薄板由于质量轻、易加工成型、工艺性能好、连接方便等特点广泛应用于机车的蒙皮[1]。但受冶金工艺的限制无法制造大面积薄板,所以蒙皮需要通过焊接连接。在焊接过程中由

【相似文献】

相关期刊论文 前3条

1 丁成钢;杨慧;;镁铝异种金属的搅拌摩擦胶接点焊[J];电焊机;2013年09期

2 胡文全;刘亚良;唐明忠;;Q235薄钢板胶接点焊工艺及性能研究[J];热加工工艺;2011年23期

3 ;[J];;年期

相关硕士学位论文 前2条

1 杨慧;AZ31/5052异种金属搅拌摩擦胶接点焊工艺及组织和性能研究[D];大连交通大学;2013年

2 倪雅琪;AZ31镁合金搅拌摩擦胶接点焊工艺研究[D];大连交通大学;2012年

，

本文编号：1423316