外加热源对铝-铜搅拌摩擦焊对接的影响

发布时间：2018-01-19 23:15

本文关键词： 搅拌摩擦焊异种合金外加热源温度场　出处：《焊接学报》2017年06期 　论文类型：期刊论文

【摘要】：为了改善铝-铜搅拌摩擦焊对接接头的焊缝接头性能,文中采用对焊缝铜一侧引入外加热源的方法,来增加焊接热输入,提高铜侧材料的软化程度.结果表明,外加热源能够有效提高焊缝部位铜一侧的焊接温度,从而增加焊接过程中铜一侧的塑化流动性,形成成形良好的焊接接头.通过焊缝的物相对比可知,外加热源引起的温度场的改变,有效地减少了焊缝中Cu Al,Cu Al2等中间相的含量,增加了铜颗粒在焊缝中的含量.在力学性能上表现为有外加热源的焊缝拉伸强度较高,显微硬度分布均匀.
[Abstract]:In order to improve the performance of Al-Cu friction stir welded butt joint, an additional heat source was introduced to the copper side of the weld to increase the welding heat input and increase the softening degree of the copper side material. The addition of heat source can effectively improve the welding temperature of the copper side of the weld, thereby increasing the plasticizing fluidity of the copper side during the welding process, forming a well-formed welding joint. The change of temperature field caused by external heat source can effectively reduce the content of Cu Al Cu Al2 and other mesophase in the weld. The content of copper particles in the weld is increased. The mechanical properties of the weld show that the tensile strength of the weld with external heat source is higher and the distribution of microhardness is uniform.
【作者单位】：南京航空航天大学材料科学与技术学院;
【基金】：国家自然科学基金资助项目(51475232) 江苏高等教育机构重点学科建设项目(PAPD) 大学研究生创新中心的基础和中央高校基本科研基金
【分类号】：TG453.9
【正文快照】： 0序言铜具有较大的导电、导热率,在电子产品的生产中占据着重要地位,可有效地提高电子元件的运行效率,同时它也具有良好的力学性能,被广泛地用作工程材料.然而较高的价格限制了铜的大规模使用,具有相似物理性能且价格低廉的铝就成为了铜的重要补充部分.复合金属结构件能够充分

【参考文献】