静轴肩辅助铝镁搅拌摩擦搭接接头的组织与性能

发布时间：2018-01-20 00:33

本文关键词： 静止轴肩搅拌摩擦搭接异种合金洋葱环金属间化合物　出处：《焊接学报》2017年04期 　论文类型：期刊论文

【摘要】：文中将静止轴肩技术应用到铝镁异种合金的搅拌摩擦搭接过程中,并分析了焊接速度对接头成形和力学性能的影响.结果表明,静止轴肩能够增强上下板之间的材料交换,焊后搅拌区呈较大的洋葱环形貌,其内部分布大量的金属间化合物;搭接面处发生良好的冶金结合.由于生成金属间化合物,洋葱环区域的显微硬度值明显高于接头其它区域.X射线衍射结果表明,金属间化合物的主要成分是Al_3Mg_2和Al_(12)Mg_(17).接头的抗拉强度随着焊接速度的增加呈先上升后下降的趋势,最大值在焊接速度为40 mm/min时取得.
[Abstract]:In this paper, the static shaft-shoulder technique is applied to the friction stir lap bonding of aluminum-magnesium dissimilar alloys, and the effect of welding speed on the forming and mechanical properties of the joints is analyzed. The static shafts can enhance the material exchange between the upper and lower plates. After welding, the stirring zone shows a larger shape of onion rings, and a large number of intermetallic compounds are distributed inside. Due to the formation of intermetallic compounds, the microhardness of onion ring region is obviously higher than that of other joints. The main components of the intermetallic compounds are Al_3Mg_2 and Altix. The tensile strength of the joints increases first and then decreases with the increase of welding speed. The maximum welding speed is 40 mm/min.
【作者单位】：哈尔滨工业大学先进焊接与连接国家重点实验室;哈尔滨工程大学材料科学与化学工程学院;
【基金】：国家自然科学基金资助项目(51204111)
【分类号】：TG453.9
【正文快照】： 0序言轻量化已在近年来受到越来越多的重视,各轻质合金的应用也越来越广泛[1].铝/镁异种合金接头具有重量低、成本低等优势,在现在工业中具有广阔的应用前景[2].然而因物理、化学性质差别较大,铝/镁异种合金的焊接难度较大.除此之外,传统熔化焊接铝/镁合金还存在接头性能低、

【相似文献】