基于应力三轴度和罗德参数的6061和7075铝合金材料断裂失效分析

发布时间：2018-01-24 23:23

本文关键词： 应力三轴度罗德参数失效应变数值模拟　出处：《实验力学》2017年03期 　论文类型：期刊论文

【摘要】：分别对6061铝合金和7075铝合金材料的缺口圆棒试件和凹槽平板试件进行准静态拉伸试验,并采用ABAQUS软件对拉伸过程进行数值模拟。模拟结果与试验测试结果吻合很好,验证了有限元模型的合理性和可靠性。通过有限元模拟,分别给出了不同试件的应力三轴度和罗德参数随等效塑性应变的变化曲线以及两种材料的失效轨迹,并对它们进行了分析讨论。结果表明:形状相同、材料性质不同的试件,应力三轴度的演化规律不同;材料的失效应变受应力三轴度和罗德参数的影响,并且不同性质的材料对罗德参数的敏感性不同。
[Abstract]:The quasi-static tensile tests of notched round bar specimens and grooved plate specimens of 6061 aluminum alloy and 7075 aluminum alloy were carried out respectively. The ABAQUS software is used to simulate the tensile process. The simulation results are in good agreement with the test results, which verify the rationality and reliability of the finite element model. The variation curves of stress triaxiality and Luo De parameters with equivalent plastic strain and the failure track of two kinds of materials are given respectively. The results show that the shape is the same. The evolution law of stress triaxiality is different for specimens with different material properties. The failure strain of the material is affected by the stress triaxiality and Luo De parameter, and the sensitivity of the material with different properties to Luo De parameter is different.
【作者单位】：太原理工大学应用力学与生物医学工程研究所;太原理工大学材料强度与结构冲击山西省重点实验室;
【基金】：国家自然科学基金(11572337) 山西省自然科学基金(201601D011011)资助
【分类号】：TG146.21
【正文快照】： 0引言自工业革命以来,金属材料在各领域的使用量迅速增长。同时,因尺寸、形状设计不合理或选材不当等,导致工程构件或机械零件发生韧性断裂而引发的意外事故也越来越普遍,对人们的生产生活造成了不可估量的损失。因此,掌握韧性金属材料的变形失效机理并建立准确的韧性断裂准则

【参考文献】