高镍铬铸钢轧辊加工用聚晶立方氮化硼刀片的制备与性能

发布时间：2018-04-20 16:01

  本文选题：聚晶立方氮化硼 + 高镍铬铸钢　； 参考：《机械工程材料》2017年12期

【摘要】：以铝钛化合物为黏结剂,制备了立方氮化硼体积分数为80%的聚晶立方氮化硼刀片,研究了其显微组织、硬度、磨损性能和切削加工性能,并与同类产品进行了对比。结果表明:所制刀片的显微硬度达到3 127 HV,显微组织分布均匀,后刀面磨损高度为0.28 mm,与同类产品的相当;断续切削时达到3.2万次冲击不崩刃,优于同类产品;在粗加工时,该刀片切削轧辊数量比同类产品的高出23%以上,在精加工时其单刃切削行程高出17%以上。
[Abstract]:Polycrystalline cubic boron nitride inserts with 80% cubic boron nitride were prepared by using aluminum and titanium compounds as binders. The microstructure, hardness, wear properties and cutting and processing properties of polycrystalline cubic boron nitride inserts were studied and compared with similar products. The results show that the microhardness of the blade is 3 127HVV, the microstructure of the blade is uniform, the wear height of the rear face is 0.28mm, which is equivalent to that of the similar products, and the impact of intermittent cutting is 32000 times, which is superior to that of the similar products. The number of cutting rollers of this blade is more than 23% higher than that of the similar products, and the cutting stroke of single blade is more than 17% higher than that of the same product during finishing.
【作者单位】： 周口师范学院机械与电气工程学院;开封贝斯科超硬材料有限公司;河南黄河旋风股份有限公司;
【基金】：国家自然科学基金资助项目(11405280) 河南省科技厅科技发展计划项目(162102310592) 周口师范学院校本项目(ZKNUB3201609)
【分类号】：TG333.17

【相似文献】

相关期刊论文 前10条

1 明之;;用聚晶立方氮化硼刀具进行加工[J];工具技术;1989年05期

2 周晓莉;;聚晶立方氮化硼陶瓷复合刀具加工淬火钢[J];机械制造;1991年07期

3 屠厚泽;聚晶立方氮化硼切削刀具的研究现状及其发展[J];探矿工程(岩土钻掘工程);1995年02期

4 刘一波，屠厚泽，，陈庆寿;聚晶立方氮化硼刀具及其制造技术综述[J];地质与勘探;1996年04期

5 肖娴;超硬工具材料在日本的应用[J];工具技术;1992年05期

6 张鹏;聚晶立方氮化硼刀具加工砂轮模具的新工艺[J];机械;1995年01期

7 ;海外科技[J];机电工程技术;2009年09期

8 张增志,张利梅,白兵占,李文龙;聚晶立方氮化硼刀具切削高锰钢的磨损机制[J];摩擦学学报;2004年03期

9 李玉标;李Z

本文编号：1778449