不锈钢车侧墙点焊铜台的爆炸焊工艺

发布时间：2018-05-14 22:07

  本文选题：不锈钢车侧墙 + 铜台　； 参考：《电焊机》2016年12期

【摘要】：采用爆炸焊工艺制造不锈钢车侧墙点焊铜台,代替了采用螺钉连接铜台合金板与基材获得的铜钢结构,避免了频繁点压铜台导致铜垫下陷的问题,提高了铜台的制作质量和产品质量。爆炸焊技术选用15 mm厚度合金铜板,节约成本50%以上,减少了合金铜板磨削时间,焊接区域能实现可靠、均匀的冶金连接,熔合率达95%以上,导电率达60%以上。
[Abstract]:The spot welding copper table on the side wall of stainless steel car was manufactured by explosive welding technology, which replaced the copper steel structure obtained by using screw to connect the copper platform alloy plate with the base material, thus avoiding the problem of copper pad sinking caused by frequent spot pressing copper table. The production quality and product quality of the copper table are improved. By using 15mm thick alloy copper plate, the cost is reduced by more than 50%, and the grinding time of alloy copper plate is reduced. The welding area can realize reliable and uniform metallurgical connection. The fusion rate is over 95% and the conductivity is over 60%.
【作者单位】： 中国中车长春轨道客车股份有限公司;
【分类号】：TG456.6

【相似文献】

相关期刊论文 前10条

1 王建民;王艳芳;张燕;;爆炸焊数值模拟研究进展[J];焊接技术;2010年07期

2 生利英;;阴极钢棒钢铝爆炸焊施工技术[J];内蒙古石油化工;2011年18期

3 ;俄罗斯爆炸焊技术的新突破[J];企业技术开发;2012年Z1期

4 藤田昌大;张丽英;;爆炸焊及其应用[J];国外舰船技术(材料类);1982年04期

5 梁希坤;爆炸焊的原理和潜能[J];铁道机车车辆工人;1996年02期

6 久保田彰;韦秀云;;爆炸焊复合材料[J];国外舰船技术(材料类);1982年03期

7 陈火金;内孔爆炸焊壳体的吸能块保护法[J];力学与实践;1980年01期

8 龚冬至;;商电铝业爆炸焊班年年安全[J];现代职业安全;2003年07期

9 ;直径为1600长为5200毫米维尼纶单体贮槽爆炸焊衬铝[J];焊接;1969年05期

10 张倩;陆铭慧;刘力博;邓燕燕;;钛合金-不锈钢爆炸焊的超声换能器制作及检测[J];无损探伤;2010年02期

相关硕士学位论文 前2条

1 吴宇;爆炸焊钛—钢结合层超声特征成像检测[D];南昌航空大学;2015年

2 赵天亮;1Cr18Ni9Ti/Q235爆炸焊参数优化数值模拟研究[D];太原科技大学;2014年

，

本文编号：1889662