烧结工艺对WC-1.0TiC-3.1TaC-4.5Co硬质合金性能及微观组织的影响

发布时间：2018-05-15 03:11

  本文选题：硬质合金 + 烧结工艺　； 参考：《材料工程》2016年12期

【摘要】：采用传统粉末冶金法,分别用真空烧结和低压烧结工艺制备出一系列WC-1.0TiC-3.1TaC-4.5Co硬质合金样品。利用光学显微镜、扫描电镜与能谱仪对合金微观组织结构特征进行观察与分析。结果表明:提高真空工艺烧结温度或采用低压烧结工艺,能使合金内部的显微孔隙、钴池减少;低压烧结制备的合金WC晶粒度小于真空烧结制备的合金WC晶粒度,合金中易出现WC晶粒异常长大现象。
[Abstract]:A series of WC-1.0TiC-3.1TaC-4.5Co cemented carbide samples were prepared by vacuum sintering and low pressure sintering by traditional powder metallurgy. The microstructure of the alloy was observed and analyzed by optical microscope, SEM and EDS. The results show that increasing the sintering temperature or adopting low pressure sintering process can reduce the micro-porosity and cobalt pool in the alloy, and the WC grain size of the alloy prepared by low-pressure sintering is smaller than that of the alloy prepared by vacuum sintering. The abnormal growth of WC grain is easy to occur in the alloy.
【作者单位】： 自贡硬质合金有限责任公司;中南大学粉末冶金国家重点实验室;
【分类号】：TG135.5

【相似文献】

相关期刊论文 前10条

1 蔡俊;丰平;贺跃辉;;烧结工艺对梯度结构硬质合金梯度层组织和厚度的影响[J];硬质合金;2007年02期

2 林宁春;无心工频化铁炉新炉衬烘烤烧结工艺的探讨[J];电炉;1990年01期

3 周亚军;张发厅;刘建秀;;烧结工艺对粉末冶金法制备镁合金摩擦磨损性能的影响[J];铸造技术;2013年12期

4 Dr.KPrzyklenk,华淑杰,王琴合;金刚石工具制造过程中的质量控制──烧结工艺的监控[J];金刚石与磨料磨具工程;1997年01期

5 周涛,周科朝,李志友,刘咏,李宇春,秦庆伟;烧结工艺对NiFeX合金性能和组织的影响[J];中国有色金属学报;2003年05期

6 韩亚苓;段春雷;古道辉;孙泰礼;;烧结工艺对衬瓷界面显微组织的影响[J];沈阳工业大学学报;2009年05期

7 王志法,许桢,姜国圣,尹志民;烧结工艺对DG合金组织和性能的影响[J];矿冶工程;1998年04期

8 俞建卫;李卫荣;焦明华;马少波;刘q;;烧结工艺对PTFE自润滑轴承材料摩擦性能的影响[J];轴承;2007年08期

9 赵，

本文编号：1890706